1050A Aluminum vs. 384.0 Aluminum
Both 1050A aluminum and 384.0 aluminum are aluminum alloys. They have 82% of their average alloy composition in common.
For each property being compared, the top bar is 1050A aluminum and the bottom bar is 384.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 20 to 45 | |
| 85 |
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 74 |
| Elongation at Break, % | 1.1 to 33 | |
| 2.5 |
| Fatigue Strength, MPa | 22 to 55 | |
| 140 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 28 |
| Shear Strength, MPa | 44 to 97 | |
| 200 |
| Tensile Strength: Ultimate (UTS), MPa | 68 to 170 | |
| 330 |
| Tensile Strength: Yield (Proof), MPa | 22 to 150 | |
| 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 550 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 170 |
| Melting Completion (Liquidus), °C | 660 | |
| 580 |
| Melting Onset (Solidus), °C | 650 | |
| 530 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 870 |
| Thermal Conductivity, W/m-K | 230 | |
| 96 |
| Thermal Expansion, µm/m-K | 24 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 59 | |
| 22 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 200 | |
| 69 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.0 | |
| 11 |
| Density, g/cm3 | 2.7 | |
| 2.9 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 7.4 |
| Embodied Energy, MJ/kg | 150 | |
| 140 |
| Embodied Water, L/kg | 1200 | |
| 1010 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 1.9 to 19 | |
| 6.9 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 3.7 to 160 | |
| 190 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 49 |
| Strength to Weight: Axial, points | 6.9 to 18 | |
| 32 |
| Strength to Weight: Bending, points | 14 to 25 | |
| 37 |
| Thermal Diffusivity, mm2/s | 94 | |
| 39 |
| Thermal Shock Resistance, points | 3.0 to 7.6 | |
| 15 |
Alloy Composition
| Aluminum (Al), % | 99.5 to 100 | |
| 77.3 to 86.5 |
| Copper (Cu), % | 0 to 0.050 | |
| 3.0 to 4.5 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 1.3 |
| Magnesium (Mg), % | 0 to 0.050 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 to 0.050 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 0 to 0.5 |
| Silicon (Si), % | 0 to 0.25 | |
| 10.5 to 12 |
| Tin (Sn), % | 0 | |
| 0 to 0.35 |
| Titanium (Ti), % | 0 to 0.050 | |
| 0 |
| Zinc (Zn), % | 0 to 0.070 | |
| 0 to 3.0 |
| Residuals, % | 0 | |
| 0 to 0.5 |