1050A Aluminum vs. EN 1.4361 Stainless Steel

1050A aluminum belongs to the aluminum alloys classification, while EN 1.4361 stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 1050A aluminum and the bottom bar is EN 1.4361 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 20 to 45
200
Elastic (Young's, Tensile) Modulus, GPa 68
190
Elongation at Break, % 1.1 to 33
43
Fatigue Strength, MPa 22 to 55
220
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 26
75
Shear Strength, MPa 44 to 97
440
Tensile Strength: Ultimate (UTS), MPa 68 to 170
630
Tensile Strength: Yield (Proof), MPa 22 to 150
250

Thermal Properties

Latent Heat of Fusion, J/g 400
350
Maximum Temperature: Mechanical, °C 170
940
Melting Completion (Liquidus), °C 660
1370
Melting Onset (Solidus), °C 650
1330
Specific Heat Capacity, J/kg-K 900
490
Thermal Conductivity, W/m-K 230
14
Thermal Expansion, µm/m-K 24
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 59
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 200
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
19
Density, g/cm3 2.7
7.6
Embodied Carbon, kg CO2/kg material 8.2
3.6
Embodied Energy, MJ/kg 150
52
Embodied Water, L/kg 1200
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 1.9 to 19
220
Resilience: Unit (Modulus of Resilience), kJ/m3 3.7 to 160
160
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
25
Strength to Weight: Axial, points 6.9 to 18
23
Strength to Weight: Bending, points 14 to 25
21
Thermal Diffusivity, mm2/s 94
3.7
Thermal Shock Resistance, points 3.0 to 7.6
15

Alloy Composition

Aluminum (Al), % 99.5 to 100
0
Carbon (C), % 0
0 to 0.015
Chromium (Cr), % 0
16.5 to 18.5
Copper (Cu), % 0 to 0.050
0
Iron (Fe), % 0 to 0.4
58.7 to 65.8
Magnesium (Mg), % 0 to 0.050
0
Manganese (Mn), % 0 to 0.050
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.2
Nickel (Ni), % 0
14 to 16
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.25
3.7 to 4.5
Sulfur (S), % 0
0 to 0.010
Titanium (Ti), % 0 to 0.050
0
Zinc (Zn), % 0 to 0.070
0