1060 Aluminum vs. 5657 Aluminum
Both 1060 aluminum and 5657 aluminum are aluminum alloys. Their average alloy composition is basically identical. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is 1060 aluminum and the bottom bar is 5657 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 68 |
| Elongation at Break, % | 1.1 to 30 | |
| 6.6 to 15 |
| Fatigue Strength, MPa | 15 to 50 | |
| 74 to 88 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 42 to 75 | |
| 92 to 110 |
| Tensile Strength: Ultimate (UTS), MPa | 67 to 130 | |
| 150 to 200 |
| Tensile Strength: Yield (Proof), MPa | 17 to 110 | |
| 140 to 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 180 |
| Melting Completion (Liquidus), °C | 660 | |
| 660 |
| Melting Onset (Solidus), °C | 650 | |
| 640 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 230 | |
| 210 |
| Thermal Expansion, µm/m-K | 24 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 62 | |
| 54 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 210 | |
| 180 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.4 |
| Embodied Energy, MJ/kg | 160 | |
| 160 |
| Embodied Water, L/kg | 1200 | |
| 1200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 0.57 to 37 | |
| 9.7 to 27 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2.1 to 89 | |
| 140 to 200 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 50 |
| Strength to Weight: Axial, points | 6.9 to 13 | |
| 15 to 20 |
| Strength to Weight: Bending, points | 14 to 21 | |
| 23 to 28 |
| Thermal Diffusivity, mm2/s | 96 | |
| 84 |
| Thermal Shock Resistance, points | 3.0 to 5.6 | |
| 6.7 to 8.6 |
Alloy Composition
| Aluminum (Al), % | 99.6 to 100 | |
| 98.5 to 99.4 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 to 0.1 |
| Gallium (Ga), % | 0 | |
| 0 to 0.030 |
| Iron (Fe), % | 0 to 0.35 | |
| 0 to 0.1 |
| Magnesium (Mg), % | 0 to 0.030 | |
| 0.6 to 1.0 |
| Manganese (Mn), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.25 | |
| 0 to 0.080 |
| Titanium (Ti), % | 0 to 0.030 | |
| 0 |
| Vanadium (V), % | 0 to 0.050 | |
| 0 to 0.050 |
| Zinc (Zn), % | 0 to 0.050 | |
| 0 to 0.050 |
| Residuals, % | 0 | |
| 0 to 0.050 |