1060 Aluminum vs. EN 1.4029 Stainless Steel

1060 aluminum belongs to the aluminum alloys classification, while EN 1.4029 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 1060 aluminum and the bottom bar is EN 1.4029 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
190
Elongation at Break, % 1.1 to 30
10 to 20
Fatigue Strength, MPa 15 to 50
270 to 400
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 26
76
Shear Strength, MPa 42 to 75
440 to 550
Tensile Strength: Ultimate (UTS), MPa 67 to 130
700 to 930
Tensile Strength: Yield (Proof), MPa 17 to 110
410 to 740

Thermal Properties

Latent Heat of Fusion, J/g 400
270
Maximum Temperature: Mechanical, °C 170
750
Melting Completion (Liquidus), °C 660
1440
Melting Onset (Solidus), °C 650
1400
Specific Heat Capacity, J/kg-K 900
480
Thermal Conductivity, W/m-K 230
30
Thermal Expansion, µm/m-K 24
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 62
3.1
Electrical Conductivity: Equal Weight (Specific), % IACS 210
3.7

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
7.0
Density, g/cm3 2.7
7.7
Embodied Carbon, kg CO2/kg material 8.3
2.0
Embodied Energy, MJ/kg 160
28
Embodied Water, L/kg 1200
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 0.57 to 37
89 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 2.1 to 89
440 to 1410
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
25
Strength to Weight: Axial, points 6.9 to 13
25 to 33
Strength to Weight: Bending, points 14 to 21
23 to 27
Thermal Diffusivity, mm2/s 96
8.1
Thermal Shock Resistance, points 3.0 to 5.6
26 to 34

Alloy Composition

Aluminum (Al), % 99.6 to 100
0
Carbon (C), % 0
0.25 to 0.32
Chromium (Cr), % 0
12 to 13.5
Copper (Cu), % 0 to 0.050
0
Iron (Fe), % 0 to 0.35
82.8 to 87.6
Magnesium (Mg), % 0 to 0.030
0
Manganese (Mn), % 0 to 0.030
0 to 1.5
Molybdenum (Mo), % 0
0 to 0.6
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.25
0 to 1.0
Sulfur (S), % 0
0.15 to 0.25
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.050
0
Zinc (Zn), % 0 to 0.050
0

Comparable Variants