1060 Aluminum vs. Solder Alloy 191

1060 aluminum belongs to the aluminum alloys classification, while solder alloy 191 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 1060 aluminum and the bottom bar is solder alloy 191.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
19
Elongation at Break, % 1.1 to 30
32
Poisson's Ratio 0.33
0.43
Shear Modulus, GPa 26
6.5
Tensile Strength: Ultimate (UTS), MPa 67 to 130
29

Thermal Properties

Latent Heat of Fusion, J/g 400
27
Melting Completion (Liquidus), °C 660
300
Melting Onset (Solidus), °C 650
300
Specific Heat Capacity, J/kg-K 900
130
Thermal Conductivity, W/m-K 230
24
Thermal Expansion, µm/m-K 24
29

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 62
8.8
Electrical Conductivity: Equal Weight (Specific), % IACS 210
7.2

Otherwise Unclassified Properties

Density, g/cm3 2.7
11
Embodied Carbon, kg CO2/kg material 8.3
5.8
Embodied Energy, MJ/kg 160
95

Common Calculations

Stiffness to Weight: Axial, points 14
0.93
Stiffness to Weight: Bending, points 50
8.0
Strength to Weight: Axial, points 6.9 to 13
0.72
Strength to Weight: Bending, points 14 to 21
1.9
Thermal Diffusivity, mm2/s 96
16
Thermal Shock Resistance, points 3.0 to 5.6
3.9

Alloy Composition

Aluminum (Al), % 99.6 to 100
0 to 0.0010
Antimony (Sb), % 0
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Copper (Cu), % 0 to 0.050
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 0.35
0 to 0.020
Lead (Pb), % 0
92.4 to 94
Magnesium (Mg), % 0 to 0.030
0
Manganese (Mn), % 0 to 0.030
0
Nickel (Ni), % 0
0 to 0.010
Silicon (Si), % 0 to 0.25
0
Silver (Ag), % 0
1.2 to 1.8
Tin (Sn), % 0
4.8 to 5.2
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.050
0
Zinc (Zn), % 0 to 0.050
0 to 0.0010