1070 Aluminum vs. EN 1.4568 Stainless Steel

1070 aluminum belongs to the aluminum alloys classification, while EN 1.4568 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 1070 aluminum and the bottom bar is EN 1.4568 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
200
Elongation at Break, % 4.5 to 39
2.3 to 21
Fatigue Strength, MPa 22 to 49
220 to 670
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 26
76
Shear Strength, MPa 48 to 79
520 to 930
Tensile Strength: Ultimate (UTS), MPa 73 to 140
830 to 1620
Tensile Strength: Yield (Proof), MPa 17 to 120
330 to 1490

Thermal Properties

Latent Heat of Fusion, J/g 400
280
Maximum Temperature: Mechanical, °C 170
890
Melting Completion (Liquidus), °C 640
1420
Melting Onset (Solidus), °C 640
1380
Specific Heat Capacity, J/kg-K 900
480
Thermal Conductivity, W/m-K 230
16
Thermal Expansion, µm/m-K 23
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 61
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 200
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
13
Density, g/cm3 2.7
7.7
Embodied Carbon, kg CO2/kg material 8.3
2.8
Embodied Energy, MJ/kg 160
40
Embodied Water, L/kg 1200
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 4.8 to 21
36 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 2.1 to 110
290 to 5710
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
25
Strength to Weight: Axial, points 7.5 to 14
30 to 58
Strength to Weight: Bending, points 14 to 22
25 to 40
Thermal Diffusivity, mm2/s 94
4.3
Thermal Shock Resistance, points 3.3 to 6.1
23 to 46

Alloy Composition

Aluminum (Al), % 99.7 to 100
0.7 to 1.5
Carbon (C), % 0
0 to 0.090
Chromium (Cr), % 0
16 to 18
Copper (Cu), % 0 to 0.040
0
Iron (Fe), % 0 to 0.25
70.9 to 76.8
Magnesium (Mg), % 0 to 0.030
0
Manganese (Mn), % 0 to 0.030
0 to 1.0
Nickel (Ni), % 0
6.5 to 7.8
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.2
0 to 0.7
Sulfur (S), % 0
0 to 0.015
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.050
0
Zinc (Zn), % 0 to 0.040
0
Residuals, % 0 to 0.030
0