1070A Aluminum vs. ASTM A369 Grade FP12

1070A aluminum belongs to the aluminum alloys classification, while ASTM A369 grade FP12 belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 1070A aluminum and the bottom bar is ASTM A369 grade FP12.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 18 to 40
140
Elastic (Young's, Tensile) Modulus, GPa 68
190
Elongation at Break, % 2.3 to 33
20
Fatigue Strength, MPa 17 to 51
170
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 26
73
Shear Strength, MPa 44 to 81
300
Tensile Strength: Ultimate (UTS), MPa 68 to 140
470
Tensile Strength: Yield (Proof), MPa 17 to 120
250

Thermal Properties

Latent Heat of Fusion, J/g 400
250
Maximum Temperature: Mechanical, °C 170
430
Melting Completion (Liquidus), °C 640
1470
Melting Onset (Solidus), °C 640
1430
Specific Heat Capacity, J/kg-K 900
470
Thermal Conductivity, W/m-K 230
45
Thermal Expansion, µm/m-K 23
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 60
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 200
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
2.8
Density, g/cm3 2.7
7.9
Embodied Carbon, kg CO2/kg material 8.2
1.6
Embodied Energy, MJ/kg 150
21
Embodied Water, L/kg 1200
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 3.0 to 18
81
Resilience: Unit (Modulus of Resilience), kJ/m3 2.1 to 100
160
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 50
24
Strength to Weight: Axial, points 7.0 to 14
17
Strength to Weight: Bending, points 14 to 22
17
Thermal Diffusivity, mm2/s 94
12
Thermal Shock Resistance, points 3.1 to 6.3
14

Alloy Composition

Aluminum (Al), % 99.7 to 100
0
Carbon (C), % 0
0.050 to 0.15
Chromium (Cr), % 0
0.8 to 1.3
Copper (Cu), % 0 to 0.030
0
Iron (Fe), % 0 to 0.25
96.8 to 98.4
Magnesium (Mg), % 0 to 0.030
0
Manganese (Mn), % 0 to 0.030
0.3 to 0.61
Molybdenum (Mo), % 0
0.44 to 0.65
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.2
0 to 0.5
Sulfur (S), % 0
0 to 0.025
Titanium (Ti), % 0 to 0.030
0
Zinc (Zn), % 0 to 0.070
0