1080A Aluminum vs. AISI 310 Stainless Steel
1080A aluminum belongs to the aluminum alloys classification, while AISI 310 stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 1080A aluminum and the bottom bar is AISI 310 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 18 to 40 | |
| 180 to 220 |
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 200 |
| Elongation at Break, % | 2.3 to 34 | |
| 34 to 45 |
| Fatigue Strength, MPa | 18 to 50 | |
| 240 to 280 |
| Poisson's Ratio | 0.33 | |
| 0.27 |
| Shear Modulus, GPa | 26 | |
| 78 |
| Shear Strength, MPa | 49 to 81 | |
| 420 to 470 |
| Tensile Strength: Ultimate (UTS), MPa | 74 to 140 | |
| 600 to 710 |
| Tensile Strength: Yield (Proof), MPa | 17 to 120 | |
| 260 to 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 1040 |
| Melting Completion (Liquidus), °C | 640 | |
| 1450 |
| Melting Onset (Solidus), °C | 640 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 480 |
| Thermal Conductivity, W/m-K | 230 | |
| 15 |
| Thermal Expansion, µm/m-K | 23 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 62 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 200 | |
| 2.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 25 |
| Density, g/cm3 | 2.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 4.3 |
| Embodied Energy, MJ/kg | 160 | |
| 61 |
| Embodied Water, L/kg | 1200 | |
| 190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 3.1 to 19 | |
| 200 to 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2.1 to 100 | |
| 170 to 310 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 25 |
| Strength to Weight: Axial, points | 7.6 to 15 | |
| 21 to 25 |
| Strength to Weight: Bending, points | 14 to 22 | |
| 20 to 22 |
| Thermal Diffusivity, mm2/s | 94 | |
| 3.9 |
| Thermal Shock Resistance, points | 3.3 to 6.4 | |
| 14 to 17 |
Alloy Composition
| Aluminum (Al), % | 99.8 to 100 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.25 |
| Chromium (Cr), % | 0 | |
| 24 to 26 |
| Copper (Cu), % | 0 to 0.030 | |
| 0 |
| Gallium (Ga), % | 0 to 0.030 | |
| 0 |
| Iron (Fe), % | 0 to 0.15 | |
| 48.2 to 57 |
| Magnesium (Mg), % | 0 to 0.020 | |
| 0 |
| Manganese (Mn), % | 0 to 0.020 | |
| 0 to 2.0 |
| Nickel (Ni), % | 0 | |
| 19 to 22 |
| Phosphorus (P), % | 0 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 0.15 | |
| 0 to 1.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 to 0.020 | |
| 0 |
| Zinc (Zn), % | 0 to 0.060 | |
| 0 |