1085 Aluminum vs. 2014 Aluminum
Both 1085 aluminum and 2014 aluminum are aluminum alloys. They have a moderately high 93% of their average alloy composition in common.
For each property being compared, the top bar is 1085 aluminum and the bottom bar is 2014 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 72 |
| Elongation at Break, % | 4.5 to 39 | |
| 1.5 to 16 |
| Fatigue Strength, MPa | 22 to 49 | |
| 90 to 160 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 27 |
| Shear Strength, MPa | 48 to 79 | |
| 130 to 290 |
| Tensile Strength: Ultimate (UTS), MPa | 73 to 140 | |
| 190 to 500 |
| Tensile Strength: Yield (Proof), MPa | 17 to 120 | |
| 100 to 440 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 210 |
| Melting Completion (Liquidus), °C | 640 | |
| 630 |
| Melting Onset (Solidus), °C | 640 | |
| 510 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 870 |
| Thermal Conductivity, W/m-K | 230 | |
| 150 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 61 | |
| 40 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 200 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 11 |
| Density, g/cm3 | 2.7 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.1 |
| Embodied Energy, MJ/kg | 160 | |
| 150 |
| Embodied Water, L/kg | 1200 | |
| 1130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.8 to 21 | |
| 6.6 to 56 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2.1 to 110 | |
| 76 to 1330 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 50 | |
| 46 |
| Strength to Weight: Axial, points | 7.5 to 14 | |
| 18 to 46 |
| Strength to Weight: Bending, points | 14 to 22 | |
| 25 to 46 |
| Thermal Diffusivity, mm2/s | 94 | |
| 58 |
| Thermal Shock Resistance, points | 3.3 to 6.1 | |
| 8.4 to 22 |
Alloy Composition
| Aluminum (Al), % | 99.85 to 100 | |
| 90.4 to 95 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.030 | |
| 3.9 to 5.0 |
| Gallium (Ga), % | 0 to 0.030 | |
| 0 |
| Iron (Fe), % | 0 to 0.12 | |
| 0 to 0.7 |
| Magnesium (Mg), % | 0 to 0.020 | |
| 0.2 to 0.8 |
| Manganese (Mn), % | 0 to 0.020 | |
| 0.4 to 1.2 |
| Silicon (Si), % | 0 to 0.1 | |
| 0.5 to 1.2 |
| Titanium (Ti), % | 0 to 0.020 | |
| 0 to 0.15 |
| Vanadium (V), % | 0 to 0.050 | |
| 0 |
| Zinc (Zn), % | 0 to 0.030 | |
| 0 to 0.25 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |