1085 Aluminum vs. 6105 Aluminum
Both 1085 aluminum and 6105 aluminum are aluminum alloys. They have a very high 98% of their average alloy composition in common.
For each property being compared, the top bar is 1085 aluminum and the bottom bar is 6105 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 68 |
| Elongation at Break, % | 4.5 to 39 | |
| 9.0 to 16 |
| Fatigue Strength, MPa | 22 to 49 | |
| 95 to 130 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 48 to 79 | |
| 120 to 170 |
| Tensile Strength: Ultimate (UTS), MPa | 73 to 140 | |
| 190 to 280 |
| Tensile Strength: Yield (Proof), MPa | 17 to 120 | |
| 120 to 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 160 |
| Melting Completion (Liquidus), °C | 640 | |
| 650 |
| Melting Onset (Solidus), °C | 640 | |
| 600 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 230 | |
| 180 to 190 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 61 | |
| 46 to 50 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 200 | |
| 150 to 170 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.3 |
| Embodied Energy, MJ/kg | 160 | |
| 150 |
| Embodied Water, L/kg | 1200 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.8 to 21 | |
| 25 to 27 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2.1 to 110 | |
| 100 to 550 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 51 |
| Strength to Weight: Axial, points | 7.5 to 14 | |
| 20 to 29 |
| Strength to Weight: Bending, points | 14 to 22 | |
| 28 to 35 |
| Thermal Diffusivity, mm2/s | 94 | |
| 72 to 79 |
| Thermal Shock Resistance, points | 3.3 to 6.1 | |
| 8.6 to 12 |
Alloy Composition
| Aluminum (Al), % | 99.85 to 100 | |
| 97.2 to 99 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.030 | |
| 0 to 0.1 |
| Gallium (Ga), % | 0 to 0.030 | |
| 0 |
| Iron (Fe), % | 0 to 0.12 | |
| 0 to 0.35 |
| Magnesium (Mg), % | 0 to 0.020 | |
| 0.45 to 0.8 |
| Manganese (Mn), % | 0 to 0.020 | |
| 0 to 0.1 |
| Silicon (Si), % | 0 to 0.1 | |
| 0.6 to 1.0 |
| Titanium (Ti), % | 0 to 0.020 | |
| 0 to 0.1 |
| Vanadium (V), % | 0 to 0.050 | |
| 0 |
| Zinc (Zn), % | 0 to 0.030 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.15 |