1200 Aluminum vs. S31803 Stainless Steel

1200 aluminum belongs to the aluminum alloys classification, while S31803 stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 1200 aluminum and the bottom bar is S31803 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 23 to 48
260
Elastic (Young's, Tensile) Modulus, GPa 69
200
Elongation at Break, % 1.1 to 28
29
Fatigue Strength, MPa 25 to 69
370
Poisson's Ratio 0.33
0.27
Shear Modulus, GPa 26
80
Shear Strength, MPa 54 to 100
460
Tensile Strength: Ultimate (UTS), MPa 85 to 180
710
Tensile Strength: Yield (Proof), MPa 28 to 160
500

Thermal Properties

Latent Heat of Fusion, J/g 400
300
Maximum Temperature: Mechanical, °C 170
1060
Melting Completion (Liquidus), °C 660
1450
Melting Onset (Solidus), °C 650
1400
Specific Heat Capacity, J/kg-K 900
480
Thermal Conductivity, W/m-K 230
16
Thermal Expansion, µm/m-K 23
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 58
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 190
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
17
Density, g/cm3 2.7
7.8
Embodied Carbon, kg CO2/kg material 8.2
3.6
Embodied Energy, MJ/kg 150
49
Embodied Water, L/kg 1190
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 2.0 to 19
180
Resilience: Unit (Modulus of Resilience), kJ/m3 5.7 to 180
630
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
25
Strength to Weight: Axial, points 8.7 to 19
25
Strength to Weight: Bending, points 16 to 26
23
Thermal Diffusivity, mm2/s 92
4.3
Thermal Shock Resistance, points 3.8 to 8.1
20

Alloy Composition

Aluminum (Al), % 99 to 100
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
21 to 23
Copper (Cu), % 0 to 0.050
0
Iron (Fe), % 0 to 1.0
63.7 to 71.9
Manganese (Mn), % 0 to 0.050
0 to 2.0
Molybdenum (Mo), % 0
2.5 to 3.5
Nickel (Ni), % 0
4.5 to 6.5
Nitrogen (N), % 0
0.080 to 0.2
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0
0 to 0.020
Titanium (Ti), % 0 to 0.050
0
Zinc (Zn), % 0 to 0.1
0
Residuals, % 0 to 0.15
0