1350 Aluminum vs. EN-MC21220 Magnesium
1350 aluminum belongs to the aluminum alloys classification, while EN-MC21220 magnesium belongs to the magnesium alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 1350 aluminum and the bottom bar is EN-MC21220 magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 20 to 45 | |
| 58 |
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 45 |
| Elongation at Break, % | 1.4 to 30 | |
| 11 |
| Fatigue Strength, MPa | 24 to 50 | |
| 89 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 17 |
| Shear Strength, MPa | 44 to 110 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 68 to 190 | |
| 210 |
| Tensile Strength: Yield (Proof), MPa | 25 to 170 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 350 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 120 |
| Melting Completion (Liquidus), °C | 660 | |
| 600 |
| Melting Onset (Solidus), °C | 650 | |
| 540 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 1000 |
| Thermal Conductivity, W/m-K | 230 | |
| 65 |
| Thermal Expansion, µm/m-K | 24 | |
| 27 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 61 to 62 | |
| 16 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 200 to 210 | |
| 87 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 12 |
| Density, g/cm3 | 2.7 | |
| 1.7 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 23 |
| Embodied Energy, MJ/kg | 160 | |
| 160 |
| Embodied Water, L/kg | 1200 | |
| 990 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 0.77 to 54 | |
| 20 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 4.4 to 200 | |
| 160 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 50 | |
| 71 |
| Strength to Weight: Axial, points | 7.0 to 19 | |
| 34 |
| Strength to Weight: Bending, points | 14 to 27 | |
| 46 |
| Thermal Diffusivity, mm2/s | 96 | |
| 39 |
| Thermal Shock Resistance, points | 3.0 to 8.2 | |
| 12 |
Alloy Composition
| Aluminum (Al), % | 99.5 to 100 | |
| 4.4 to 5.5 |
| Boron (B), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 0 to 0.010 | |
| 0 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 to 0.010 |
| Gallium (Ga), % | 0 to 0.030 | |
| 0 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.0050 |
| Magnesium (Mg), % | 0 | |
| 93.5 to 95.5 |
| Manganese (Mn), % | 0 to 0.010 | |
| 0.1 to 0.6 |
| Nickel (Ni), % | 0 | |
| 0 to 0.0020 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0 to 0.020 | |
| 0 |
| Vanadium (V), % | 0 to 0.020 | |
| 0 |
| Zinc (Zn), % | 0 to 0.050 | |
| 0 to 0.3 |
| Residuals, % | 0 | |
| 0 to 0.010 |