1435 Aluminum vs. 713.0 Aluminum

Both 1435 aluminum and 713.0 aluminum are aluminum alloys. They have a moderately high 91% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is 1435 aluminum and the bottom bar is 713.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 69
71
Elongation at Break, % 4.1 to 32
3.9 to 4.3
Fatigue Strength, MPa 27 to 49
63 to 120
Poisson's Ratio 0.33
0.32
Shear Modulus, GPa 26
27
Shear Strength, MPa 54 to 87
180
Tensile Strength: Ultimate (UTS), MPa 81 to 150
240 to 260
Tensile Strength: Yield (Proof), MPa 23 to 130
170

Thermal Properties

Latent Heat of Fusion, J/g 400
370
Maximum Temperature: Mechanical, °C 170
180
Melting Completion (Liquidus), °C 650
630
Melting Onset (Solidus), °C 640
610
Specific Heat Capacity, J/kg-K 900
860
Thermal Conductivity, W/m-K 230
150
Thermal Expansion, µm/m-K 23
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 60
35
Electrical Conductivity: Equal Weight (Specific), % IACS 200
100

Otherwise Unclassified Properties

Base Metal Price, % relative 9.0
9.5
Density, g/cm3 2.7
3.1
Embodied Carbon, kg CO2/kg material 8.2
7.8
Embodied Energy, MJ/kg 150
150
Embodied Water, L/kg 1190
1110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.0 to 20
8.7 to 9.9
Resilience: Unit (Modulus of Resilience), kJ/m3 3.8 to 110
210 to 220
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 50
45
Strength to Weight: Axial, points 8.3 to 15
22 to 23
Strength to Weight: Bending, points 15 to 23
28 to 29
Thermal Diffusivity, mm2/s 93
57
Thermal Shock Resistance, points 3.6 to 6.7
10 to 11

Alloy Composition

Aluminum (Al), % 99.35 to 99.7
87.6 to 92.4
Chromium (Cr), % 0
0 to 0.35
Copper (Cu), % 0 to 0.020
0.4 to 1.0
Iron (Fe), % 0.3 to 0.5
0 to 1.1
Magnesium (Mg), % 0 to 0.050
0.2 to 0.5
Manganese (Mn), % 0 to 0.050
0 to 0.6
Nickel (Ni), % 0
0 to 0.15
Silicon (Si), % 0 to 0.15
0 to 0.25
Titanium (Ti), % 0 to 0.030
0 to 0.25
Zinc (Zn), % 0 to 0.1
7.0 to 8.0
Residuals, % 0
0 to 0.25