2007 Aluminum vs. EN 1.3553 Steel

2007 aluminum belongs to the aluminum alloys classification, while EN 1.3553 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 2007 aluminum and the bottom bar is EN 1.3553 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 71
200
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 27
77
Tensile Strength: Ultimate (UTS), MPa 370 to 420
720

Thermal Properties

Latent Heat of Fusion, J/g 390
260
Maximum Temperature: Mechanical, °C 190
540
Melting Completion (Liquidus), °C 640
1620
Melting Onset (Solidus), °C 510
1570
Specific Heat Capacity, J/kg-K 870
440
Thermal Conductivity, W/m-K 130
24
Thermal Expansion, µm/m-K 23
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 47
10
Electrical Conductivity: Equal Weight (Specific), % IACS 140
11

Otherwise Unclassified Properties

Base Metal Price, % relative 11
24
Density, g/cm3 3.1
8.4
Embodied Carbon, kg CO2/kg material 8.0
8.5
Embodied Energy, MJ/kg 150
130
Embodied Water, L/kg 1130
96

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 44
23
Strength to Weight: Axial, points 33 to 38
24
Strength to Weight: Bending, points 37 to 40
21
Thermal Diffusivity, mm2/s 48
6.4
Thermal Shock Resistance, points 16 to 19
21

Alloy Composition

Aluminum (Al), % 87.5 to 95
0
Bismuth (Bi), % 0 to 0.2
0
Carbon (C), % 0
0.78 to 0.86
Chromium (Cr), % 0 to 0.1
3.9 to 4.3
Copper (Cu), % 3.3 to 4.6
0 to 0.3
Iron (Fe), % 0 to 0.8
80.7 to 83.7
Lead (Pb), % 0.8 to 1.5
0
Magnesium (Mg), % 0.4 to 1.8
0
Manganese (Mn), % 0.5 to 1.0
0 to 0.4
Molybdenum (Mo), % 0
4.7 to 5.2
Nickel (Ni), % 0 to 0.2
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.8
0 to 0.4
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 0 to 0.2
0
Titanium (Ti), % 0 to 0.2
0
Tungsten (W), % 0
6.0 to 6.7
Vanadium (V), % 0
1.7 to 2.0
Zinc (Zn), % 0 to 0.8
0
Residuals, % 0 to 0.3
0