2007 Aluminum vs. EN AC-45300 Aluminum
Both 2007 aluminum and EN AC-45300 aluminum are aluminum alloys. They have a moderately high 94% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is 2007 aluminum and the bottom bar is EN AC-45300 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 71 |
| Elongation at Break, % | 5.6 to 8.0 | |
| 1.0 to 2.8 |
| Fatigue Strength, MPa | 91 to 110 | |
| 59 to 72 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 370 to 420 | |
| 220 to 290 |
| Tensile Strength: Yield (Proof), MPa | 240 to 270 | |
| 150 to 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 470 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 170 |
| Melting Completion (Liquidus), °C | 640 | |
| 630 |
| Melting Onset (Solidus), °C | 510 | |
| 590 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 890 |
| Thermal Conductivity, W/m-K | 130 | |
| 150 |
| Thermal Expansion, µm/m-K | 23 | |
| 22 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 47 | |
| 36 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 9.5 |
| Density, g/cm3 | 3.1 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 8.0 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1130 | |
| 1120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 26 | |
| 2.7 to 5.6 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 390 to 530 | |
| 160 to 390 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 44 | |
| 50 |
| Strength to Weight: Axial, points | 33 to 38 | |
| 23 to 29 |
| Strength to Weight: Bending, points | 37 to 40 | |
| 30 to 35 |
| Thermal Diffusivity, mm2/s | 48 | |
| 60 |
| Thermal Shock Resistance, points | 16 to 19 | |
| 10 to 13 |
Alloy Composition
| Aluminum (Al), % | 87.5 to 95 | |
| 90.2 to 94.2 |
| Bismuth (Bi), % | 0 to 0.2 | |
| 0 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 3.3 to 4.6 | |
| 1.0 to 1.5 |
| Iron (Fe), % | 0 to 0.8 | |
| 0 to 0.65 |
| Lead (Pb), % | 0.8 to 1.5 | |
| 0 to 0.15 |
| Magnesium (Mg), % | 0.4 to 1.8 | |
| 0.35 to 0.65 |
| Manganese (Mn), % | 0.5 to 1.0 | |
| 0 to 0.55 |
| Nickel (Ni), % | 0 to 0.2 | |
| 0 to 0.25 |
| Silicon (Si), % | 0 to 0.8 | |
| 4.5 to 5.5 |
| Tin (Sn), % | 0 to 0.2 | |
| 0 to 0.050 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 to 0.8 | |
| 0 to 0.15 |
| Residuals, % | 0 | |
| 0 to 0.15 |