2014 Aluminum vs. 5088 Aluminum
Both 2014 aluminum and 5088 aluminum are aluminum alloys. They have a moderately high 94% of their average alloy composition in common.
For each property being compared, the top bar is 2014 aluminum and the bottom bar is 5088 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 72 | |
| 68 |
| Elongation at Break, % | 1.5 to 16 | |
| 29 |
| Fatigue Strength, MPa | 90 to 160 | |
| 180 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 25 |
| Shear Strength, MPa | 130 to 290 | |
| 200 |
| Tensile Strength: Ultimate (UTS), MPa | 190 to 500 | |
| 310 |
| Tensile Strength: Yield (Proof), MPa | 100 to 440 | |
| 150 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 200 |
| Melting Completion (Liquidus), °C | 630 | |
| 640 |
| Melting Onset (Solidus), °C | 510 | |
| 540 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 900 |
| Thermal Conductivity, W/m-K | 150 | |
| 120 |
| Thermal Expansion, µm/m-K | 23 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 40 | |
| 29 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 98 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 9.5 |
| Density, g/cm3 | 3.0 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.1 | |
| 9.0 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1130 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.6 to 56 | |
| 76 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 76 to 1330 | |
| 170 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 46 | |
| 50 |
| Strength to Weight: Axial, points | 18 to 46 | |
| 32 |
| Strength to Weight: Bending, points | 25 to 46 | |
| 38 |
| Thermal Diffusivity, mm2/s | 58 | |
| 51 |
| Thermal Shock Resistance, points | 8.4 to 22 | |
| 14 |
Alloy Composition
| Aluminum (Al), % | 90.4 to 95 | |
| 92.4 to 94.8 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 to 0.15 |
| Copper (Cu), % | 3.9 to 5.0 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 0.7 | |
| 0.1 to 0.35 |
| Magnesium (Mg), % | 0.2 to 0.8 | |
| 4.7 to 5.5 |
| Manganese (Mn), % | 0.4 to 1.2 | |
| 0.2 to 0.5 |
| Silicon (Si), % | 0.5 to 1.2 | |
| 0 to 0.2 |
| Titanium (Ti), % | 0 to 0.15 | |
| 0 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0.2 to 0.4 |
| Zirconium (Zr), % | 0 to 0.2 | |
| 0 to 0.15 |
| Residuals, % | 0 | |
| 0 to 0.15 |