2014A Aluminum vs. EN 1.4962 Stainless Steel
2014A aluminum belongs to the aluminum alloys classification, while EN 1.4962 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 2014A aluminum and the bottom bar is EN 1.4962 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 72 | |
| 200 |
| Elongation at Break, % | 6.2 to 16 | |
| 22 to 34 |
| Fatigue Strength, MPa | 93 to 150 | |
| 210 to 330 |
| Poisson's Ratio | 0.33 | |
| 0.28 |
| Shear Modulus, GPa | 27 | |
| 77 |
| Shear Strength, MPa | 130 to 290 | |
| 420 to 440 |
| Tensile Strength: Ultimate (UTS), MPa | 210 to 490 | |
| 630 to 690 |
| Tensile Strength: Yield (Proof), MPa | 110 to 430 | |
| 260 to 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 910 |
| Melting Completion (Liquidus), °C | 640 | |
| 1480 |
| Melting Onset (Solidus), °C | 510 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 470 |
| Thermal Conductivity, W/m-K | 150 | |
| 14 |
| Thermal Expansion, µm/m-K | 23 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 37 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 2.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 23 |
| Density, g/cm3 | 3.0 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 8.1 | |
| 4.1 |
| Embodied Energy, MJ/kg | 150 | |
| 59 |
| Embodied Water, L/kg | 1140 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 to 49 | |
| 140 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 85 to 1300 | |
| 170 to 610 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 46 | |
| 24 |
| Strength to Weight: Axial, points | 19 to 45 | |
| 21 to 24 |
| Strength to Weight: Bending, points | 26 to 46 | |
| 20 to 21 |
| Thermal Diffusivity, mm2/s | 55 | |
| 3.7 |
| Thermal Shock Resistance, points | 9.0 to 22 | |
| 14 to 16 |
Alloy Composition
| Aluminum (Al), % | 90.8 to 95 | |
| 0 |
| Boron (B), % | 0 | |
| 0.0015 to 0.0060 |
| Carbon (C), % | 0 | |
| 0.070 to 0.15 |
| Chromium (Cr), % | 0 to 0.1 | |
| 15.5 to 17.5 |
| Copper (Cu), % | 3.9 to 5.0 | |
| 0 |
| Iron (Fe), % | 0 to 0.5 | |
| 62.1 to 69 |
| Magnesium (Mg), % | 0.2 to 0.8 | |
| 0 |
| Manganese (Mn), % | 0.4 to 1.2 | |
| 0 to 1.5 |
| Nickel (Ni), % | 0 to 0.1 | |
| 12.5 to 14.5 |
| Phosphorus (P), % | 0 | |
| 0 to 0.035 |
| Silicon (Si), % | 0.5 to 0.9 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 to 0.15 | |
| 0.4 to 0.7 |
| Tungsten (W), % | 0 | |
| 2.5 to 3.0 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.2 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 |