2017A Aluminum vs. Grade 1 Babbitt Metal
2017A aluminum belongs to the aluminum alloys classification, while grade 1 Babbitt Metal belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 2017A aluminum and the bottom bar is grade 1 Babbitt Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 53 |
| Elongation at Break, % | 2.2 to 14 | |
| 34 |
| Poisson's Ratio | 0.33 | |
| 0.35 |
| Shear Modulus, GPa | 27 | |
| 20 |
| Tensile Strength: Yield (Proof), MPa | 110 to 290 | |
| 30 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 70 |
| Melting Completion (Liquidus), °C | 650 | |
| 370 |
| Melting Onset (Solidus), °C | 510 | |
| 220 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 230 |
| Thermal Conductivity, W/m-K | 150 | |
| 45 |
| Thermal Expansion, µm/m-K | 23 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 34 | |
| 13 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 100 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 75 |
| Density, g/cm3 | 3.0 | |
| 7.3 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 12 |
| Embodied Energy, MJ/kg | 150 | |
| 200 |
| Embodied Water, L/kg | 1140 | |
| 1160 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 90 to 570 | |
| 8.6 |
| Stiffness to Weight: Axial, points | 13 | |
| 4.0 |
| Stiffness to Weight: Bending, points | 46 | |
| 17 |
| Thermal Diffusivity, mm2/s | 56 | |
| 26 |
Alloy Composition
| Aluminum (Al), % | 91.3 to 95.5 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 4.0 to 5.0 |
| Arsenic (As), % | 0 | |
| 0 to 0.1 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.080 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 3.5 to 4.5 | |
| 4.0 to 5.0 |
| Iron (Fe), % | 0 to 0.7 | |
| 0 to 0.080 |
| Lead (Pb), % | 0 | |
| 0 to 0.35 |
| Magnesium (Mg), % | 0.4 to 1.0 | |
| 0 |
| Manganese (Mn), % | 0.4 to 1.0 | |
| 0 |
| Silicon (Si), % | 0.2 to 0.8 | |
| 0 |
| Tin (Sn), % | 0 | |
| 89.3 to 92 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.0050 |
| Zirconium (Zr), % | 0 to 0.25 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 |