2017A Aluminum vs. SAE-AISI 1541 Steel
2017A aluminum belongs to the aluminum alloys classification, while SAE-AISI 1541 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 2017A aluminum and the bottom bar is SAE-AISI 1541 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 190 |
| Elongation at Break, % | 2.2 to 14 | |
| 11 to 17 |
| Fatigue Strength, MPa | 92 to 130 | |
| 260 to 420 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 27 | |
| 73 |
| Shear Strength, MPa | 120 to 270 | |
| 440 to 480 |
| Tensile Strength: Ultimate (UTS), MPa | 200 to 460 | |
| 720 to 790 |
| Tensile Strength: Yield (Proof), MPa | 110 to 290 | |
| 390 to 680 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 400 |
| Melting Completion (Liquidus), °C | 650 | |
| 1460 |
| Melting Onset (Solidus), °C | 510 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 470 |
| Thermal Conductivity, W/m-K | 150 | |
| 52 |
| Thermal Expansion, µm/m-K | 23 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 34 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 100 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 1.9 |
| Density, g/cm3 | 3.0 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 1.4 |
| Embodied Energy, MJ/kg | 150 | |
| 19 |
| Embodied Water, L/kg | 1140 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.7 to 53 | |
| 78 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 90 to 570 | |
| 410 to 1250 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 46 | |
| 24 |
| Strength to Weight: Axial, points | 19 to 42 | |
| 25 to 28 |
| Strength to Weight: Bending, points | 26 to 44 | |
| 23 to 24 |
| Thermal Diffusivity, mm2/s | 56 | |
| 14 |
| Thermal Shock Resistance, points | 8.9 to 20 | |
| 23 to 25 |
Alloy Composition
| Aluminum (Al), % | 91.3 to 95.5 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.36 to 0.44 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 3.5 to 4.5 | |
| 0 |
| Iron (Fe), % | 0 to 0.7 | |
| 97.8 to 98.3 |
| Magnesium (Mg), % | 0.4 to 1.0 | |
| 0 |
| Manganese (Mn), % | 0.4 to 1.0 | |
| 1.4 to 1.7 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.2 to 0.8 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.050 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.25 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 |