2036 Aluminum vs. 6012 Aluminum
Both 2036 aluminum and 6012 aluminum are aluminum alloys. They have a very high 97% of their average alloy composition in common.
For each property being compared, the top bar is 2036 aluminum and the bottom bar is 6012 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 69 |
| Elongation at Break, % | 24 | |
| 9.1 to 11 |
| Fatigue Strength, MPa | 130 | |
| 55 to 100 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 210 | |
| 130 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 340 | |
| 220 to 320 |
| Tensile Strength: Yield (Proof), MPa | 200 | |
| 110 to 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 170 |
| Melting Completion (Liquidus), °C | 650 | |
| 640 |
| Melting Onset (Solidus), °C | 560 | |
| 570 |
| Specific Heat Capacity, J/kg-K | 890 | |
| 890 |
| Thermal Conductivity, W/m-K | 160 | |
| 160 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 41 | |
| 45 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 130 | |
| 140 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 9.5 |
| Density, g/cm3 | 2.9 | |
| 2.9 |
| Embodied Carbon, kg CO2/kg material | 8.1 | |
| 8.2 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1160 | |
| 1170 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 70 | |
| 21 to 28 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 270 | |
| 94 to 480 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 48 | |
| 48 |
| Strength to Weight: Axial, points | 33 | |
| 22 to 32 |
| Strength to Weight: Bending, points | 38 | |
| 29 to 37 |
| Thermal Diffusivity, mm2/s | 62 | |
| 62 |
| Thermal Shock Resistance, points | 15 | |
| 10 to 14 |
Alloy Composition
| Aluminum (Al), % | 94.4 to 97.4 | |
| 92.2 to 98 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.7 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 to 0.3 |
| Copper (Cu), % | 2.2 to 3.0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.5 |
| Lead (Pb), % | 0 | |
| 0.4 to 2.0 |
| Magnesium (Mg), % | 0.3 to 0.6 | |
| 0.6 to 1.2 |
| Manganese (Mn), % | 0.1 to 0.4 | |
| 0.4 to 1.0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0.6 to 1.4 |
| Titanium (Ti), % | 0 to 0.15 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.3 |
| Residuals, % | 0 | |
| 0 to 0.15 |