2124 Aluminum vs. 5082 Aluminum
Both 2124 aluminum and 5082 aluminum are aluminum alloys. They have a very high 95% of their average alloy composition in common.
For each property being compared, the top bar is 2124 aluminum and the bottom bar is 5082 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 67 |
| Elongation at Break, % | 5.7 | |
| 1.1 |
| Fatigue Strength, MPa | 130 | |
| 110 to 130 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 25 |
| Shear Strength, MPa | 280 | |
| 210 to 230 |
| Tensile Strength: Ultimate (UTS), MPa | 490 | |
| 380 to 400 |
| Tensile Strength: Yield (Proof), MPa | 430 | |
| 300 to 340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 180 |
| Melting Completion (Liquidus), °C | 640 | |
| 640 |
| Melting Onset (Solidus), °C | 500 | |
| 560 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 910 |
| Thermal Conductivity, W/m-K | 150 | |
| 130 |
| Thermal Expansion, µm/m-K | 23 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 38 | |
| 32 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 9.5 |
| Density, g/cm3 | 3.0 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 8.9 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1150 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 27 | |
| 4.0 to 4.3 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1290 | |
| 670 to 870 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 46 | |
| 51 |
| Strength to Weight: Axial, points | 45 | |
| 39 to 41 |
| Strength to Weight: Bending, points | 46 | |
| 43 to 45 |
| Thermal Diffusivity, mm2/s | 58 | |
| 54 |
| Thermal Shock Resistance, points | 21 | |
| 17 to 18 |
Alloy Composition
| Aluminum (Al), % | 91.3 to 94.7 | |
| 93.5 to 96 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 to 0.15 |
| Copper (Cu), % | 3.8 to 4.9 | |
| 0 to 0.15 |
| Iron (Fe), % | 0 to 0.3 | |
| 0 to 0.35 |
| Magnesium (Mg), % | 1.2 to 1.8 | |
| 4.0 to 5.0 |
| Manganese (Mn), % | 0.3 to 0.9 | |
| 0 to 0.15 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.2 |
| Titanium (Ti), % | 0 to 0.15 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |