2218 Aluminum vs. 6105 Aluminum
Both 2218 aluminum and 6105 aluminum are aluminum alloys. They have a moderately high 93% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 2218 aluminum and the bottom bar is 6105 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 73 | |
| 68 |
| Elongation at Break, % | 6.8 to 10 | |
| 9.0 to 16 |
| Fatigue Strength, MPa | 110 | |
| 95 to 130 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 26 |
| Shear Strength, MPa | 210 to 250 | |
| 120 to 170 |
| Tensile Strength: Ultimate (UTS), MPa | 330 to 430 | |
| 190 to 280 |
| Tensile Strength: Yield (Proof), MPa | 260 to 310 | |
| 120 to 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 160 |
| Melting Completion (Liquidus), °C | 640 | |
| 650 |
| Melting Onset (Solidus), °C | 510 | |
| 600 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 900 |
| Thermal Conductivity, W/m-K | 140 | |
| 180 to 190 |
| Thermal Expansion, µm/m-K | 22 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 37 | |
| 46 to 50 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 150 to 170 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 9.5 |
| Density, g/cm3 | 3.1 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 8.3 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1130 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 27 to 31 | |
| 25 to 27 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 450 to 650 | |
| 100 to 550 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 45 | |
| 51 |
| Strength to Weight: Axial, points | 30 to 39 | |
| 20 to 29 |
| Strength to Weight: Bending, points | 34 to 41 | |
| 28 to 35 |
| Thermal Diffusivity, mm2/s | 52 | |
| 72 to 79 |
| Thermal Shock Resistance, points | 15 to 19 | |
| 8.6 to 12 |
Alloy Composition
| Aluminum (Al), % | 88.8 to 93.6 | |
| 97.2 to 99 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 to 0.1 |
| Copper (Cu), % | 3.5 to 4.5 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 0.35 |
| Magnesium (Mg), % | 1.2 to 1.8 | |
| 0.45 to 0.8 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 to 0.1 |
| Nickel (Ni), % | 1.7 to 2.3 | |
| 0 |
| Silicon (Si), % | 0 to 0.9 | |
| 0.6 to 1.0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.15 |