5005A Aluminum vs. 5457 Aluminum
Both 5005A aluminum and 5457 aluminum are aluminum alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is 5005A aluminum and the bottom bar is 5457 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 29 to 64 | |
| 32 to 55 |
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 68 |
| Elongation at Break, % | 1.1 to 21 | |
| 6.0 to 22 |
| Fatigue Strength, MPa | 38 to 82 | |
| 55 to 98 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 71 to 130 | |
| 85 to 130 |
| Tensile Strength: Ultimate (UTS), MPa | 110 to 230 | |
| 130 to 210 |
| Tensile Strength: Yield (Proof), MPa | 43 to 210 | |
| 50 to 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 180 |
| Melting Completion (Liquidus), °C | 660 | |
| 660 |
| Melting Onset (Solidus), °C | 630 | |
| 630 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 200 | |
| 180 |
| Thermal Expansion, µm/m-K | 24 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 52 | |
| 46 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 170 | |
| 150 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.4 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1190 | |
| 1190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.0 to 19 | |
| 12 to 23 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 14 to 310 | |
| 18 to 250 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 50 |
| Strength to Weight: Axial, points | 12 to 24 | |
| 13 to 21 |
| Strength to Weight: Bending, points | 19 to 31 | |
| 21 to 28 |
| Thermal Diffusivity, mm2/s | 82 | |
| 72 |
| Thermal Shock Resistance, points | 5.0 to 10 | |
| 5.7 to 9.0 |
Alloy Composition
| Aluminum (Al), % | 97.5 to 99.3 | |
| 97.8 to 99.05 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 0.45 | |
| 0 to 0.1 |
| Magnesium (Mg), % | 0.7 to 1.1 | |
| 0.8 to 1.2 |
| Manganese (Mn), % | 0 to 0.15 | |
| 0.15 to 0.45 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 0.080 |
| Vanadium (V), % | 0 | |
| 0 to 0.050 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 to 0.050 |
| Residuals, % | 0 | |
| 0 to 0.1 |