5005A Aluminum vs. Grade CW6M Nickel

5005A aluminum belongs to the aluminum alloys classification, while grade CW6M nickel belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 5005A aluminum and the bottom bar is grade CW6M nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
220
Elongation at Break, % 1.1 to 21
29
Fatigue Strength, MPa 38 to 82
210
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 26
84
Tensile Strength: Ultimate (UTS), MPa 110 to 230
560
Tensile Strength: Yield (Proof), MPa 43 to 210
310

Thermal Properties

Latent Heat of Fusion, J/g 400
330
Maximum Temperature: Mechanical, °C 180
970
Melting Completion (Liquidus), °C 660
1530
Melting Onset (Solidus), °C 630
1470
Specific Heat Capacity, J/kg-K 900
430
Thermal Expansion, µm/m-K 24
12

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
65
Density, g/cm3 2.7
8.8
Embodied Carbon, kg CO2/kg material 8.3
13
Embodied Energy, MJ/kg 150
170
Embodied Water, L/kg 1190
300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 2.0 to 19
140
Resilience: Unit (Modulus of Resilience), kJ/m3 14 to 310
220
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
23
Strength to Weight: Axial, points 12 to 24
18
Strength to Weight: Bending, points 19 to 31
17
Thermal Shock Resistance, points 5.0 to 10
16

Alloy Composition

Aluminum (Al), % 97.5 to 99.3
0
Carbon (C), % 0
0 to 0.070
Chromium (Cr), % 0 to 0.1
17 to 20
Copper (Cu), % 0 to 0.050
0
Iron (Fe), % 0 to 0.45
0 to 3.0
Magnesium (Mg), % 0.7 to 1.1
0
Manganese (Mn), % 0 to 0.15
0 to 1.0
Molybdenum (Mo), % 0
17 to 20
Nickel (Ni), % 0
54.9 to 66
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.3
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 0 to 0.2
0
Residuals, % 0 to 0.15
0