5010 Aluminum vs. CC334G Bronze

5010 aluminum belongs to the aluminum alloys classification, while CC334G bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 5010 aluminum and the bottom bar is CC334G bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 27 to 62
210
Elastic (Young's, Tensile) Modulus, GPa 69
120
Elongation at Break, % 1.1 to 23
5.6
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 26
45
Tensile Strength: Ultimate (UTS), MPa 100 to 210
810
Tensile Strength: Yield (Proof), MPa 38 to 190
410

Thermal Properties

Latent Heat of Fusion, J/g 400
240
Maximum Temperature: Mechanical, °C 180
240
Melting Completion (Liquidus), °C 650
1080
Melting Onset (Solidus), °C 630
1020
Specific Heat Capacity, J/kg-K 900
450
Thermal Conductivity, W/m-K 200
41
Thermal Expansion, µm/m-K 23
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 45
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 150
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
29
Density, g/cm3 2.7
8.2
Embodied Carbon, kg CO2/kg material 8.2
3.6
Embodied Energy, MJ/kg 150
59
Embodied Water, L/kg 1190
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 2.3 to 20
38
Resilience: Unit (Modulus of Resilience), kJ/m3 10 to 270
710
Stiffness to Weight: Axial, points 14
8.1
Stiffness to Weight: Bending, points 50
20
Strength to Weight: Axial, points 10 to 22
28
Strength to Weight: Bending, points 18 to 29
24
Thermal Diffusivity, mm2/s 82
11
Thermal Shock Resistance, points 4.5 to 9.4
28

Alloy Composition

Aluminum (Al), % 97.1 to 99.7
10 to 12
Chromium (Cr), % 0 to 0.15
0
Copper (Cu), % 0 to 0.25
72 to 84.5
Iron (Fe), % 0 to 0.7
3.0 to 7.0
Lead (Pb), % 0
0 to 0.050
Magnesium (Mg), % 0.2 to 0.6
0 to 0.050
Manganese (Mn), % 0.1 to 0.3
0 to 2.5
Nickel (Ni), % 0
4.0 to 7.5
Silicon (Si), % 0 to 0.4
0 to 0.1
Tin (Sn), % 0
0 to 0.2
Titanium (Ti), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.3
0 to 0.5
Residuals, % 0 to 0.15
0