5010 Aluminum vs. SAE-AISI 4028 Steel
5010 aluminum belongs to the aluminum alloys classification, while SAE-AISI 4028 steel belongs to the iron alloys. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 5010 aluminum and the bottom bar is SAE-AISI 4028 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 27 to 62 | |
| 150 to 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 190 |
| Elongation at Break, % | 1.1 to 23 | |
| 14 to 23 |
| Fatigue Strength, MPa | 35 to 83 | |
| 180 to 330 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 73 |
| Shear Strength, MPa | 64 to 120 | |
| 310 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 100 to 210 | |
| 490 to 630 |
| Tensile Strength: Yield (Proof), MPa | 38 to 190 | |
| 260 to 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 400 |
| Melting Completion (Liquidus), °C | 650 | |
| 1460 |
| Melting Onset (Solidus), °C | 630 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 470 |
| Thermal Conductivity, W/m-K | 200 | |
| 49 |
| Thermal Expansion, µm/m-K | 23 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 45 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 150 | |
| 8.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 2.1 |
| Density, g/cm3 | 2.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 1.5 |
| Embodied Energy, MJ/kg | 150 | |
| 19 |
| Embodied Water, L/kg | 1190 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.3 to 20 | |
| 81 to 95 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 10 to 270 | |
| 180 to 720 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 50 | |
| 24 |
| Strength to Weight: Axial, points | 10 to 22 | |
| 17 to 22 |
| Strength to Weight: Bending, points | 18 to 29 | |
| 18 to 21 |
| Thermal Diffusivity, mm2/s | 82 | |
| 13 |
| Thermal Shock Resistance, points | 4.5 to 9.4 | |
| 16 to 20 |
Alloy Composition
| Aluminum (Al), % | 97.1 to 99.7 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.25 to 0.3 |
| Chromium (Cr), % | 0 to 0.15 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 0 to 0.7 | |
| 98.1 to 98.7 |
| Magnesium (Mg), % | 0.2 to 0.6 | |
| 0 |
| Manganese (Mn), % | 0.1 to 0.3 | |
| 0.7 to 0.9 |
| Molybdenum (Mo), % | 0 | |
| 0.2 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 0.4 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 | |
| 0.035 to 0.050 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.3 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 |