5021 Aluminum vs. EN 1.4443 Stainless Steel

5021 aluminum belongs to the aluminum alloys classification, while EN 1.4443 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 5021 aluminum and the bottom bar is EN 1.4443 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 68
200
Elongation at Break, % 1.1 to 3.4
34
Fatigue Strength, MPa 85 to 110
170
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 26
78
Tensile Strength: Ultimate (UTS), MPa 300 to 310
490
Tensile Strength: Yield (Proof), MPa 240 to 270
210

Thermal Properties

Latent Heat of Fusion, J/g 400
300
Maximum Temperature: Mechanical, °C 180
1000
Melting Completion (Liquidus), °C 640
1440
Melting Onset (Solidus), °C 590
1400
Specific Heat Capacity, J/kg-K 900
470
Thermal Conductivity, W/m-K 140
15
Thermal Expansion, µm/m-K 23
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 35
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 120
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
20
Density, g/cm3 2.7
7.9
Embodied Carbon, kg CO2/kg material 8.6
4.0
Embodied Energy, MJ/kg 150
54
Embodied Water, L/kg 1180
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 3.1 to 10
140
Resilience: Unit (Modulus of Resilience), kJ/m3 440 to 550
110
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
25
Strength to Weight: Axial, points 30 to 32
17
Strength to Weight: Bending, points 37
18
Thermal Diffusivity, mm2/s 57
3.9
Thermal Shock Resistance, points 13 to 14
11

Alloy Composition

Aluminum (Al), % 95.2 to 97.7
0
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0 to 0.15
18 to 20
Copper (Cu), % 0 to 0.15
0
Iron (Fe), % 0 to 0.5
60.4 to 69.5
Magnesium (Mg), % 2.2 to 2.8
0
Manganese (Mn), % 0.1 to 0.5
0 to 2.0
Molybdenum (Mo), % 0
2.5 to 3.0
Nickel (Ni), % 0
10 to 13
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.5
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 0 to 0.15
0
Residuals, % 0 to 0.15
0