5021 Aluminum vs. Grade 36 Titanium
5021 aluminum belongs to the aluminum alloys classification, while grade 36 titanium belongs to the titanium alloys. There are 25 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 5021 aluminum and the bottom bar is grade 36 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 110 |
| Elongation at Break, % | 1.1 to 3.4 | |
| 11 |
| Fatigue Strength, MPa | 85 to 110 | |
| 300 |
| Poisson's Ratio | 0.33 | |
| 0.36 |
| Shear Modulus, GPa | 26 | |
| 39 |
| Shear Strength, MPa | 170 | |
| 320 |
| Tensile Strength: Ultimate (UTS), MPa | 300 to 310 | |
| 530 |
| Tensile Strength: Yield (Proof), MPa | 240 to 270 | |
| 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 370 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 320 |
| Melting Completion (Liquidus), °C | 640 | |
| 2020 |
| Melting Onset (Solidus), °C | 590 | |
| 1950 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 420 |
| Thermal Expansion, µm/m-K | 23 | |
| 8.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.7 | |
| 6.3 |
| Embodied Carbon, kg CO2/kg material | 8.6 | |
| 58 |
| Embodied Energy, MJ/kg | 150 | |
| 920 |
| Embodied Water, L/kg | 1180 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 3.1 to 10 | |
| 59 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 440 to 550 | |
| 1260 |
| Stiffness to Weight: Axial, points | 14 | |
| 9.3 |
| Stiffness to Weight: Bending, points | 50 | |
| 25 |
| Strength to Weight: Axial, points | 30 to 32 | |
| 23 |
| Strength to Weight: Bending, points | 37 | |
| 23 |
| Thermal Shock Resistance, points | 13 to 14 | |
| 45 |
Alloy Composition
| Aluminum (Al), % | 95.2 to 97.7 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 to 0.15 | |
| 0 |
| Copper (Cu), % | 0 to 0.15 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0035 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.030 |
| Magnesium (Mg), % | 2.2 to 2.8 | |
| 0 |
| Manganese (Mn), % | 0.1 to 0.5 | |
| 0 |
| Niobium (Nb), % | 0 | |
| 42 to 47 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.16 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 52.3 to 58 |
| Zinc (Zn), % | 0 to 0.15 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |