5049 Aluminum vs. 515.0 Aluminum

Both 5049 aluminum and 515.0 aluminum are aluminum alloys. They have a very high 98% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is 5049 aluminum and the bottom bar is 515.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 69
70
Elongation at Break, % 2.0 to 18
10
Fatigue Strength, MPa 79 to 130
130
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 26
26
Shear Strength, MPa 130 to 190
190
Tensile Strength: Ultimate (UTS), MPa 210 to 330
280

Thermal Properties

Latent Heat of Fusion, J/g 400
470
Maximum Temperature: Mechanical, °C 190
170
Melting Completion (Liquidus), °C 650
620
Melting Onset (Solidus), °C 620
620
Specific Heat Capacity, J/kg-K 900
900
Thermal Expansion, µm/m-K 24
23

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
9.5
Density, g/cm3 2.7
2.6
Embodied Carbon, kg CO2/kg material 8.5
8.4
Embodied Energy, MJ/kg 150
150
Embodied Water, L/kg 1180
1120

Common Calculations

Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 50
52
Strength to Weight: Axial, points 22 to 34
30
Strength to Weight: Bending, points 29 to 39
36
Thermal Shock Resistance, points 9.3 to 15
13

Alloy Composition

Aluminum (Al), % 94.7 to 97.9
93.6 to 96.6
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.1
0 to 0.2
Iron (Fe), % 0 to 0.5
0 to 1.3
Magnesium (Mg), % 1.6 to 2.5
2.5 to 4.0
Manganese (Mn), % 0.5 to 1.1
0.4 to 0.6
Silicon (Si), % 0 to 0.4
0.5 to 10
Titanium (Ti), % 0 to 0.1
0
Zinc (Zn), % 0 to 0.2
0 to 0.1
Residuals, % 0
0 to 0.15