5052 Aluminum vs. EN 1.3541 Stainless Steel

5052 aluminum belongs to the aluminum alloys classification, while EN 1.3541 stainless steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 5052 aluminum and the bottom bar is EN 1.3541 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 46 to 83
220
Elastic (Young's, Tensile) Modulus, GPa 68
190
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 26
76
Tensile Strength: Ultimate (UTS), MPa 190 to 320
710

Thermal Properties

Latent Heat of Fusion, J/g 400
270
Maximum Temperature: Mechanical, °C 190
770
Melting Completion (Liquidus), °C 650
1440
Melting Onset (Solidus), °C 610
1390
Specific Heat Capacity, J/kg-K 900
480
Thermal Conductivity, W/m-K 140
30
Thermal Expansion, µm/m-K 24
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 35
3.0
Electrical Conductivity: Equal Weight (Specific), % IACS 120
3.5

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
7.0
Density, g/cm3 2.7
7.7
Embodied Carbon, kg CO2/kg material 8.6
1.9
Embodied Energy, MJ/kg 150
27
Embodied Water, L/kg 1190
100

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 50
25
Strength to Weight: Axial, points 19 to 33
26
Strength to Weight: Bending, points 27 to 38
23
Thermal Diffusivity, mm2/s 57
8.1
Thermal Shock Resistance, points 8.3 to 14
26

Alloy Composition

Aluminum (Al), % 95.8 to 97.7
0
Carbon (C), % 0
0.43 to 0.5
Chromium (Cr), % 0.15 to 0.35
12.5 to 14.5
Copper (Cu), % 0 to 0.1
0
Iron (Fe), % 0 to 0.4
83.4 to 87.5
Magnesium (Mg), % 2.2 to 2.8
0
Manganese (Mn), % 0 to 0.1
0 to 1.0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.25
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 0 to 0.1
0
Residuals, % 0 to 0.15
0