5059 Aluminum vs. C65100 Bronze
5059 aluminum belongs to the aluminum alloys classification, while C65100 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 5059 aluminum and the bottom bar is C65100 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 120 |
| Elongation at Break, % | 11 to 25 | |
| 2.4 to 50 |
| Poisson's Ratio | 0.33 | |
| 0.34 |
| Shear Modulus, GPa | 26 | |
| 43 |
| Shear Strength, MPa | 220 to 250 | |
| 200 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 350 to 410 | |
| 280 to 560 |
| Tensile Strength: Yield (Proof), MPa | 170 to 300 | |
| 95 to 440 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 200 |
| Melting Completion (Liquidus), °C | 650 | |
| 1060 |
| Melting Onset (Solidus), °C | 510 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 390 |
| Thermal Conductivity, W/m-K | 110 | |
| 57 |
| Thermal Expansion, µm/m-K | 24 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 29 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 95 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 30 |
| Density, g/cm3 | 2.7 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 9.1 | |
| 2.6 |
| Embodied Energy, MJ/kg | 160 | |
| 41 |
| Embodied Water, L/kg | 1160 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 42 to 75 | |
| 12 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 to 650 | |
| 39 to 820 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 50 | |
| 18 |
| Strength to Weight: Axial, points | 36 to 42 | |
| 8.7 to 18 |
| Strength to Weight: Bending, points | 41 to 45 | |
| 11 to 17 |
| Thermal Diffusivity, mm2/s | 44 | |
| 16 |
| Thermal Shock Resistance, points | 16 to 18 | |
| 9.5 to 19 |
Alloy Composition
| Aluminum (Al), % | 89.9 to 94 | |
| 0 |
| Chromium (Cr), % | 0 to 0.25 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 94.5 to 99.2 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.8 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Magnesium (Mg), % | 5.0 to 6.0 | |
| 0 |
| Manganese (Mn), % | 0.6 to 1.2 | |
| 0 to 0.7 |
| Silicon (Si), % | 0 to 0.45 | |
| 0.8 to 2.0 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 |
| Zinc (Zn), % | 0.4 to 0.9 | |
| 0 to 1.5 |
| Zirconium (Zr), % | 0.050 to 0.25 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |