5082 Aluminum vs. 7178 Aluminum
Both 5082 aluminum and 7178 aluminum are aluminum alloys. They have a moderately high 91% of their average alloy composition in common.
For each property being compared, the top bar is 5082 aluminum and the bottom bar is 7178 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 67 | |
| 71 |
| Elongation at Break, % | 1.1 | |
| 4.5 to 12 |
| Fatigue Strength, MPa | 110 to 130 | |
| 120 to 210 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 25 | |
| 27 |
| Shear Strength, MPa | 210 to 230 | |
| 140 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 400 | |
| 240 to 640 |
| Tensile Strength: Yield (Proof), MPa | 300 to 340 | |
| 120 to 560 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 370 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 180 |
| Melting Completion (Liquidus), °C | 640 | |
| 630 |
| Melting Onset (Solidus), °C | 560 | |
| 480 |
| Specific Heat Capacity, J/kg-K | 910 | |
| 860 |
| Thermal Conductivity, W/m-K | 130 | |
| 130 |
| Thermal Expansion, µm/m-K | 24 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 32 | |
| 31 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 91 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 10 |
| Density, g/cm3 | 2.7 | |
| 3.1 |
| Embodied Carbon, kg CO2/kg material | 8.9 | |
| 8.2 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1180 | |
| 1110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.0 to 4.3 | |
| 24 to 52 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 670 to 870 | |
| 110 to 2220 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 51 | |
| 45 |
| Strength to Weight: Axial, points | 39 to 41 | |
| 21 to 58 |
| Strength to Weight: Bending, points | 43 to 45 | |
| 28 to 54 |
| Thermal Diffusivity, mm2/s | 54 | |
| 47 |
| Thermal Shock Resistance, points | 17 to 18 | |
| 10 to 28 |
Alloy Composition
| Aluminum (Al), % | 93.5 to 96 | |
| 85.4 to 89.5 |
| Chromium (Cr), % | 0 to 0.15 | |
| 0.18 to 0.28 |
| Copper (Cu), % | 0 to 0.15 | |
| 1.6 to 2.4 |
| Iron (Fe), % | 0 to 0.35 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 4.0 to 5.0 | |
| 2.4 to 3.1 |
| Manganese (Mn), % | 0 to 0.15 | |
| 0 to 0.3 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.4 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 to 0.25 | |
| 6.3 to 7.3 |
| Residuals, % | 0 | |
| 0 to 0.15 |