5082 Aluminum vs. C67400 Bronze
5082 aluminum belongs to the aluminum alloys classification, while C67400 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 5082 aluminum and the bottom bar is C67400 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 67 | |
| 110 |
| Elongation at Break, % | 1.1 | |
| 22 to 28 |
| Poisson's Ratio | 0.33 | |
| 0.31 |
| Shear Modulus, GPa | 25 | |
| 41 |
| Shear Strength, MPa | 210 to 230 | |
| 310 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 400 | |
| 480 to 610 |
| Tensile Strength: Yield (Proof), MPa | 300 to 340 | |
| 250 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 130 |
| Melting Completion (Liquidus), °C | 640 | |
| 890 |
| Melting Onset (Solidus), °C | 560 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 910 | |
| 400 |
| Thermal Conductivity, W/m-K | 130 | |
| 100 |
| Thermal Expansion, µm/m-K | 24 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 32 | |
| 23 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 23 |
| Density, g/cm3 | 2.7 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 8.9 | |
| 2.8 |
| Embodied Energy, MJ/kg | 150 | |
| 48 |
| Embodied Water, L/kg | 1180 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.0 to 4.3 | |
| 110 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 670 to 870 | |
| 300 to 660 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 51 | |
| 20 |
| Strength to Weight: Axial, points | 39 to 41 | |
| 17 to 22 |
| Strength to Weight: Bending, points | 43 to 45 | |
| 17 to 20 |
| Thermal Diffusivity, mm2/s | 54 | |
| 32 |
| Thermal Shock Resistance, points | 17 to 18 | |
| 16 to 20 |
Alloy Composition
| Aluminum (Al), % | 93.5 to 96 | |
| 0.5 to 2.0 |
| Chromium (Cr), % | 0 to 0.15 | |
| 0 |
| Copper (Cu), % | 0 to 0.15 | |
| 57 to 60 |
| Iron (Fe), % | 0 to 0.35 | |
| 0 to 0.35 |
| Lead (Pb), % | 0 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 4.0 to 5.0 | |
| 0 |
| Manganese (Mn), % | 0 to 0.15 | |
| 2.0 to 3.5 |
| Nickel (Ni), % | 0 | |
| 0 to 0.25 |
| Silicon (Si), % | 0 to 0.2 | |
| 0.5 to 1.5 |
| Tin (Sn), % | 0 | |
| 0 to 0.3 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.25 | |
| 31.1 to 40 |
| Residuals, % | 0 | |
| 0 to 0.5 |