5083 Aluminum vs. 2014 Aluminum
Both 5083 aluminum and 2014 aluminum are aluminum alloys. They have a moderately high 95% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is 5083 aluminum and the bottom bar is 2014 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 72 |
| Elongation at Break, % | 1.1 to 17 | |
| 1.5 to 16 |
| Fatigue Strength, MPa | 93 to 190 | |
| 90 to 160 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 27 |
| Shear Strength, MPa | 170 to 220 | |
| 130 to 290 |
| Tensile Strength: Ultimate (UTS), MPa | 290 to 390 | |
| 190 to 500 |
| Tensile Strength: Yield (Proof), MPa | 110 to 340 | |
| 100 to 440 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 210 |
| Melting Completion (Liquidus), °C | 640 | |
| 630 |
| Melting Onset (Solidus), °C | 580 | |
| 510 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 870 |
| Thermal Conductivity, W/m-K | 120 | |
| 150 |
| Thermal Expansion, µm/m-K | 24 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 29 | |
| 40 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 96 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 11 |
| Density, g/cm3 | 2.7 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 8.9 | |
| 8.1 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1170 | |
| 1130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.2 to 42 | |
| 6.6 to 56 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 95 to 860 | |
| 76 to 1330 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 50 | |
| 46 |
| Strength to Weight: Axial, points | 29 to 40 | |
| 18 to 46 |
| Strength to Weight: Bending, points | 36 to 44 | |
| 25 to 46 |
| Thermal Diffusivity, mm2/s | 48 | |
| 58 |
| Thermal Shock Resistance, points | 12 to 17 | |
| 8.4 to 22 |
Alloy Composition
| Aluminum (Al), % | 92.4 to 95.6 | |
| 90.4 to 95 |
| Chromium (Cr), % | 0.050 to 0.25 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.1 | |
| 3.9 to 5.0 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.7 |
| Magnesium (Mg), % | 4.0 to 4.9 | |
| 0.2 to 0.8 |
| Manganese (Mn), % | 0.4 to 1.0 | |
| 0.4 to 1.2 |
| Silicon (Si), % | 0 to 0.4 | |
| 0.5 to 1.2 |
| Titanium (Ti), % | 0 to 0.15 | |
| 0 to 0.15 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.25 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |