5083 Aluminum vs. 5021 Aluminum
Both 5083 aluminum and 5021 aluminum are aluminum alloys. They have a very high 97% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is 5083 aluminum and the bottom bar is 5021 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 68 |
| Elongation at Break, % | 1.1 to 17 | |
| 1.1 to 3.4 |
| Fatigue Strength, MPa | 93 to 190 | |
| 85 to 110 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 170 to 220 | |
| 170 |
| Tensile Strength: Ultimate (UTS), MPa | 290 to 390 | |
| 300 to 310 |
| Tensile Strength: Yield (Proof), MPa | 110 to 340 | |
| 240 to 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 180 |
| Melting Completion (Liquidus), °C | 640 | |
| 640 |
| Melting Onset (Solidus), °C | 580 | |
| 590 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 120 | |
| 140 |
| Thermal Expansion, µm/m-K | 24 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 29 | |
| 35 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 96 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.9 | |
| 8.6 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1170 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.2 to 42 | |
| 3.1 to 10 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 95 to 860 | |
| 440 to 550 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 50 |
| Strength to Weight: Axial, points | 29 to 40 | |
| 30 to 32 |
| Strength to Weight: Bending, points | 36 to 44 | |
| 37 |
| Thermal Diffusivity, mm2/s | 48 | |
| 57 |
| Thermal Shock Resistance, points | 12 to 17 | |
| 13 to 14 |
Alloy Composition
| Aluminum (Al), % | 92.4 to 95.6 | |
| 95.2 to 97.7 |
| Chromium (Cr), % | 0.050 to 0.25 | |
| 0 to 0.15 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 to 0.15 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 4.0 to 4.9 | |
| 2.2 to 2.8 |
| Manganese (Mn), % | 0.4 to 1.0 | |
| 0.1 to 0.5 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.4 |
| Titanium (Ti), % | 0 to 0.15 | |
| 0 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.15 |
| Residuals, % | 0 | |
| 0 to 0.15 |