50Cr-50Ni-Cb Alloy vs. 7020 Aluminum
50Cr-50Ni-Cb alloy belongs to the otherwise unclassified metals classification, while 7020 aluminum belongs to the aluminum alloys. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 50Cr-50Ni-Cb alloy and the bottom bar is 7020 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 70 |
| Elongation at Break, % | 5.6 | |
| 8.4 to 14 |
| Poisson's Ratio | 0.26 | |
| 0.33 |
| Shear Modulus, GPa | 84 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 190 to 390 |
| Tensile Strength: Yield (Proof), MPa | 390 | |
| 120 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 880 |
| Thermal Expansion, µm/m-K | 15 | |
| 23 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 9.5 |
| Density, g/cm3 | 8.0 | |
| 2.9 |
| Embodied Carbon, kg CO2/kg material | 9.2 | |
| 8.3 |
| Embodied Energy, MJ/kg | 130 | |
| 150 |
| Embodied Water, L/kg | 350 | |
| 1150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 30 | |
| 23 to 46 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 370 | |
| 110 to 690 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 47 |
| Strength to Weight: Axial, points | 21 | |
| 18 to 37 |
| Strength to Weight: Bending, points | 20 | |
| 25 to 41 |
| Thermal Shock Resistance, points | 14 | |
| 8.3 to 17 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.25 | |
| 91.2 to 94.8 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Chromium (Cr), % | 47 to 52 | |
| 0.1 to 0.35 |
| Copper (Cu), % | 0 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 0.4 |
| Magnesium (Mg), % | 0 | |
| 1.0 to 1.4 |
| Manganese (Mn), % | 0 to 0.3 | |
| 0.050 to 0.5 |
| Nickel (Ni), % | 43.3 to 51.6 | |
| 0 |
| Niobium (Nb), % | 1.4 to 1.7 | |
| 0 |
| Nitrogen (N), % | 0 to 0.16 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.35 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 |
| Titanium (Ti), % | 0 to 0.5 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 | |
| 4.0 to 5.0 |
| Zirconium (Zr), % | 0 | |
| 0.080 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |