50Cr-50Ni-Cb Alloy vs. ASTM A210 Steel

50Cr-50Ni-Cb alloy belongs to the otherwise unclassified metals classification, while ASTM A210 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is 50Cr-50Ni-Cb alloy and the bottom bar is ASTM A210 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 5.6
34
Poisson's Ratio 0.26
0.29
Shear Modulus, GPa 84
73
Tensile Strength: Ultimate (UTS), MPa 620
470 to 540
Tensile Strength: Yield (Proof), MPa 390
290 to 310

Thermal Properties

Latent Heat of Fusion, J/g 350
250
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 15
12

Otherwise Unclassified Properties

Base Metal Price, % relative 60
1.8
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 9.2
1.4
Embodied Energy, MJ/kg 130
18
Embodied Water, L/kg 350
45 to 46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 30
140 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 370
230 to 250
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
17 to 19
Strength to Weight: Bending, points 20
17 to 19
Thermal Shock Resistance, points 14
15 to 17