50Cr-50Ni-Cb Alloy vs. EN 1.4938 Stainless Steel
50Cr-50Ni-Cb alloy belongs to the otherwise unclassified metals classification, while EN 1.4938 stainless steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is 50Cr-50Ni-Cb alloy and the bottom bar is EN 1.4938 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 200 |
| Elongation at Break, % | 5.6 | |
| 16 to 17 |
| Poisson's Ratio | 0.26 | |
| 0.28 |
| Shear Modulus, GPa | 84 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 870 to 1030 |
| Tensile Strength: Yield (Proof), MPa | 390 | |
| 640 to 870 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 270 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Expansion, µm/m-K | 15 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 10 |
| Density, g/cm3 | 8.0 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 9.2 | |
| 3.3 |
| Embodied Energy, MJ/kg | 130 | |
| 47 |
| Embodied Water, L/kg | 350 | |
| 110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 30 | |
| 140 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 370 | |
| 1050 to 1920 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 21 | |
| 31 to 37 |
| Strength to Weight: Bending, points | 20 | |
| 26 to 29 |
| Thermal Shock Resistance, points | 14 | |
| 30 to 35 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.25 | |
| 0 |
| Carbon (C), % | 0 to 0.1 | |
| 0.080 to 0.15 |
| Chromium (Cr), % | 47 to 52 | |
| 11 to 12.5 |
| Iron (Fe), % | 0 to 1.0 | |
| 80.5 to 84.8 |
| Manganese (Mn), % | 0 to 0.3 | |
| 0.4 to 0.9 |
| Molybdenum (Mo), % | 0 | |
| 1.5 to 2.0 |
| Nickel (Ni), % | 43.3 to 51.6 | |
| 2.0 to 3.0 |
| Niobium (Nb), % | 1.4 to 1.7 | |
| 0 |
| Nitrogen (N), % | 0 to 0.16 | |
| 0.020 to 0.040 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 to 0.5 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.25 to 0.4 |