50Cr-50Ni-Cb Alloy vs. EN 1.5521 Steel
50Cr-50Ni-Cb alloy belongs to the otherwise unclassified metals classification, while EN 1.5521 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is 50Cr-50Ni-Cb alloy and the bottom bar is EN 1.5521 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 5.6 | |
| 11 to 21 |
| Poisson's Ratio | 0.26 | |
| 0.29 |
| Shear Modulus, GPa | 84 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 430 to 1390 |
| Tensile Strength: Yield (Proof), MPa | 390 | |
| 300 to 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Expansion, µm/m-K | 15 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 60 | |
| 1.9 |
| Density, g/cm3 | 8.0 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 9.2 | |
| 1.4 |
| Embodied Energy, MJ/kg | 130 | |
| 19 |
| Embodied Water, L/kg | 350 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 30 | |
| 44 to 230 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 370 | |
| 250 to 630 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 21 | |
| 15 to 49 |
| Strength to Weight: Bending, points | 20 | |
| 16 to 35 |
| Thermal Shock Resistance, points | 14 | |
| 13 to 41 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.25 | |
| 0 |
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0 to 0.1 | |
| 0.16 to 0.2 |
| Chromium (Cr), % | 47 to 52 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 1.0 | |
| 98 to 98.9 |
| Manganese (Mn), % | 0 to 0.3 | |
| 0.9 to 1.2 |
| Nickel (Ni), % | 43.3 to 51.6 | |
| 0 |
| Niobium (Nb), % | 1.4 to 1.7 | |
| 0 |
| Nitrogen (N), % | 0 to 0.16 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.025 |
| Titanium (Ti), % | 0 to 0.5 | |
| 0 |