50Cr-50Ni Alloy vs. AWS E317L

50Cr-50Ni alloy belongs to the otherwise unclassified metals classification, while AWS E317L belongs to the iron alloys. They have a modest 34% of their average alloy composition in common, which, by itself, doesn't mean much. There are 18 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is 50Cr-50Ni alloy and the bottom bar is AWS E317L.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 5.7
34
Poisson's Ratio 0.26
0.28
Shear Modulus, GPa 84
79
Tensile Strength: Ultimate (UTS), MPa 620
580

Thermal Properties

Latent Heat of Fusion, J/g 350
300
Specific Heat Capacity, J/kg-K 490
470
Thermal Expansion, µm/m-K 15
14

Otherwise Unclassified Properties

Base Metal Price, % relative 50
22
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 7.9
4.3
Embodied Energy, MJ/kg 110
59
Embodied Water, L/kg 350
170

Common Calculations

Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
20
Strength to Weight: Bending, points 20
20
Thermal Shock Resistance, points 14
15

Alloy Composition

Aluminum (Al), % 0 to 0.25
0
Carbon (C), % 0 to 0.1
0 to 0.040
Chromium (Cr), % 48 to 52
18 to 21
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 0 to 1.0
56.6 to 66.5
Manganese (Mn), % 0 to 0.3
0.5 to 2.5
Molybdenum (Mo), % 0
3.0 to 4.0
Nickel (Ni), % 44.5 to 52
12 to 14
Nitrogen (N), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.030
Titanium (Ti), % 0 to 0.5
0