50Cr-50Ni Alloy vs. AWS E320LR

50Cr-50Ni alloy belongs to the otherwise unclassified metals classification, while AWS E320LR belongs to the iron alloys. They have 55% of their average alloy composition in common. There are 18 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is 50Cr-50Ni alloy and the bottom bar is AWS E320LR.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 5.7
34
Poisson's Ratio 0.26
0.28
Shear Modulus, GPa 84
77
Tensile Strength: Ultimate (UTS), MPa 620
580

Thermal Properties

Latent Heat of Fusion, J/g 350
300
Specific Heat Capacity, J/kg-K 490
460
Thermal Expansion, µm/m-K 15
14

Otherwise Unclassified Properties

Base Metal Price, % relative 50
36
Density, g/cm3 8.0
8.2
Embodied Carbon, kg CO2/kg material 7.9
6.2
Embodied Energy, MJ/kg 110
87
Embodied Water, L/kg 350
220

Common Calculations

Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
20
Strength to Weight: Bending, points 20
19
Thermal Shock Resistance, points 14
15

Alloy Composition

Aluminum (Al), % 0 to 0.25
0
Carbon (C), % 0 to 0.1
0 to 0.030
Chromium (Cr), % 48 to 52
19 to 21
Copper (Cu), % 0
3.0 to 4.0
Iron (Fe), % 0 to 1.0
32.7 to 42.5
Manganese (Mn), % 0 to 0.3
1.5 to 2.5
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 44.5 to 52
32 to 36
Niobium (Nb), % 0
0 to 0.4
Nitrogen (N), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.020
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.020
0 to 0.015
Titanium (Ti), % 0 to 0.5
0