50Cr-50Ni Alloy vs. SAE-AISI 5140 Steel
50Cr-50Ni alloy belongs to the otherwise unclassified metals classification, while SAE-AISI 5140 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is 50Cr-50Ni alloy and the bottom bar is SAE-AISI 5140 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 5.7 | |
| 12 to 29 |
| Poisson's Ratio | 0.26 | |
| 0.29 |
| Shear Modulus, GPa | 84 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 560 to 970 |
| Tensile Strength: Yield (Proof), MPa | 390 | |
| 290 to 840 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 470 |
| Thermal Expansion, µm/m-K | 15 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 50 | |
| 2.1 |
| Density, g/cm3 | 8.0 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 7.9 | |
| 1.4 |
| Embodied Energy, MJ/kg | 110 | |
| 19 |
| Embodied Water, L/kg | 350 | |
| 49 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 31 | |
| 76 to 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 350 | |
| 220 to 1880 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 21 | |
| 20 to 34 |
| Strength to Weight: Bending, points | 20 | |
| 19 to 28 |
| Thermal Shock Resistance, points | 14 | |
| 16 to 29 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.25 | |
| 0 |
| Carbon (C), % | 0 to 0.1 | |
| 0.38 to 0.43 |
| Chromium (Cr), % | 48 to 52 | |
| 0.7 to 0.9 |
| Iron (Fe), % | 0 to 1.0 | |
| 97.3 to 98.1 |
| Manganese (Mn), % | 0 to 0.3 | |
| 0.7 to 0.9 |
| Nickel (Ni), % | 44.5 to 52 | |
| 0 |
| Nitrogen (N), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.040 |
| Titanium (Ti), % | 0 to 0.5 | |
| 0 |