5110A Aluminum vs. 224.0 Aluminum
Both 5110A aluminum and 224.0 aluminum are aluminum alloys. They have a moderately high 94% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 5110A aluminum and the bottom bar is 224.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 71 |
| Elongation at Break, % | 4.5 to 28 | |
| 4.0 to 10 |
| Fatigue Strength, MPa | 37 to 77 | |
| 86 to 120 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 100 to 190 | |
| 380 to 420 |
| Tensile Strength: Yield (Proof), MPa | 32 to 170 | |
| 280 to 330 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 220 |
| Melting Completion (Liquidus), °C | 640 | |
| 650 |
| Melting Onset (Solidus), °C | 640 | |
| 550 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 870 |
| Thermal Conductivity, W/m-K | 220 | |
| 120 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 57 | |
| 32 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 190 | |
| 95 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 11 |
| Density, g/cm3 | 2.7 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 8.3 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1190 | |
| 1150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.8 to 22 | |
| 16 to 35 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 7.6 to 200 | |
| 540 to 770 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 50 | |
| 45 |
| Strength to Weight: Axial, points | 10 to 19 | |
| 35 to 38 |
| Strength to Weight: Bending, points | 18 to 27 | |
| 38 to 41 |
| Thermal Diffusivity, mm2/s | 91 | |
| 47 |
| Thermal Shock Resistance, points | 4.5 to 8.4 | |
| 17 to 18 |
Alloy Composition
| Aluminum (Al), % | 98.5 to 99.8 | |
| 93 to 95.2 |
| Copper (Cu), % | 0 to 0.2 | |
| 4.5 to 5.5 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.1 |
| Magnesium (Mg), % | 0.2 to 0.6 | |
| 0 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0.2 to 0.5 |
| Silicon (Si), % | 0 to 0.15 | |
| 0 to 0.060 |
| Titanium (Ti), % | 0 | |
| 0 to 0.35 |
| Vanadium (V), % | 0 | |
| 0.050 to 0.15 |
| Zinc (Zn), % | 0 to 0.030 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0.1 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.1 |