5154A Aluminum vs. Nickel 30
5154A aluminum belongs to the aluminum alloys classification, while nickel 30 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 5154A aluminum and the bottom bar is nickel 30.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 210 |
| Elongation at Break, % | 1.1 to 19 | |
| 34 |
| Fatigue Strength, MPa | 83 to 160 | |
| 200 |
| Poisson's Ratio | 0.33 | |
| 0.28 |
| Shear Modulus, GPa | 26 | |
| 82 |
| Shear Strength, MPa | 140 to 210 | |
| 440 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 370 | |
| 660 |
| Tensile Strength: Yield (Proof), MPa | 96 to 320 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 1020 |
| Melting Completion (Liquidus), °C | 650 | |
| 1480 |
| Melting Onset (Solidus), °C | 600 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 450 |
| Thermal Conductivity, W/m-K | 130 | |
| 10 |
| Thermal Expansion, µm/m-K | 24 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 32 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 1.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 60 |
| Density, g/cm3 | 2.7 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 8.8 | |
| 9.4 |
| Embodied Energy, MJ/kg | 150 | |
| 130 |
| Embodied Water, L/kg | 1180 | |
| 290 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.0 to 36 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 68 to 760 | |
| 180 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 51 | |
| 23 |
| Strength to Weight: Axial, points | 24 to 38 | |
| 22 |
| Strength to Weight: Bending, points | 31 to 43 | |
| 20 |
| Thermal Diffusivity, mm2/s | 53 | |
| 2.7 |
| Thermal Shock Resistance, points | 10 to 16 | |
| 18 |
Alloy Composition
| Aluminum (Al), % | 93.7 to 96.9 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 to 0.25 | |
| 28 to 31.5 |
| Cobalt (Co), % | 0 | |
| 0 to 5.0 |
| Copper (Cu), % | 0 to 0.1 | |
| 1.0 to 2.4 |
| Iron (Fe), % | 0 to 0.5 | |
| 13 to 17 |
| Magnesium (Mg), % | 3.1 to 3.9 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 to 0.030 |
| Molybdenum (Mo), % | 0 | |
| 4.0 to 6.0 |
| Nickel (Ni), % | 0 | |
| 30.2 to 52.2 |
| Niobium (Nb), % | 0 | |
| 0.3 to 1.5 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.8 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 |
| Tungsten (W), % | 0 | |
| 1.5 to 4.0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 |