5182 Aluminum vs. EN 1.1191 Steel
5182 aluminum belongs to the aluminum alloys classification, while EN 1.1191 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 5182 aluminum and the bottom bar is EN 1.1191 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 190 |
| Elongation at Break, % | 1.1 to 12 | |
| 16 to 17 |
| Fatigue Strength, MPa | 100 to 130 | |
| 210 to 290 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 25 | |
| 72 |
| Shear Strength, MPa | 170 to 240 | |
| 380 to 430 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 420 | |
| 630 to 700 |
| Tensile Strength: Yield (Proof), MPa | 130 to 360 | |
| 310 to 440 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 400 |
| Melting Completion (Liquidus), °C | 640 | |
| 1460 |
| Melting Onset (Solidus), °C | 590 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 470 |
| Thermal Conductivity, W/m-K | 130 | |
| 48 |
| Thermal Expansion, µm/m-K | 24 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 94 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 2.1 |
| Density, g/cm3 | 2.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 8.9 | |
| 1.4 |
| Embodied Energy, MJ/kg | 150 | |
| 19 |
| Embodied Water, L/kg | 1180 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.6 to 49 | |
| 83 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 950 | |
| 260 to 510 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 51 | |
| 24 |
| Strength to Weight: Axial, points | 29 to 44 | |
| 22 to 25 |
| Strength to Weight: Bending, points | 36 to 47 | |
| 21 to 22 |
| Thermal Diffusivity, mm2/s | 53 | |
| 13 |
| Thermal Shock Resistance, points | 12 to 19 | |
| 20 to 22 |
Alloy Composition
| Aluminum (Al), % | 93.2 to 95.8 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.42 to 0.5 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 to 0.4 |
| Copper (Cu), % | 0 to 0.15 | |
| 0 |
| Iron (Fe), % | 0 to 0.35 | |
| 97.3 to 99.08 |
| Magnesium (Mg), % | 4.0 to 5.0 | |
| 0 |
| Manganese (Mn), % | 0.2 to 0.5 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 | |
| 0 to 0.4 |
| Phosphorus (P), % | 0 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 | |
| 0 to 0.035 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 |