5182 Aluminum vs. K93603 Alloy
5182 aluminum belongs to the aluminum alloys classification, while K93603 alloy belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 5182 aluminum and the bottom bar is K93603 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 190 |
| Poisson's Ratio | 0.33 | |
| 0.3 |
| Shear Modulus, GPa | 25 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 280 to 420 | |
| 490 to 810 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 270 |
| Melting Completion (Liquidus), °C | 640 | |
| 1430 |
| Melting Onset (Solidus), °C | 590 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 460 |
| Thermal Expansion, µm/m-K | 24 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 25 |
| Density, g/cm3 | 2.7 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 8.9 | |
| 4.8 |
| Embodied Energy, MJ/kg | 150 | |
| 66 |
| Embodied Water, L/kg | 1180 | |
| 120 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 51 | |
| 23 |
| Strength to Weight: Axial, points | 29 to 44 | |
| 17 to 27 |
| Strength to Weight: Bending, points | 36 to 47 | |
| 17 to 24 |
| Thermal Shock Resistance, points | 12 to 19 | |
| 15 to 25 |
Alloy Composition
| Aluminum (Al), % | 93.2 to 95.8 | |
| 0 to 0.1 |
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 to 0.25 |
| Cobalt (Co), % | 0 | |
| 0 to 0.5 |
| Copper (Cu), % | 0 to 0.15 | |
| 0 |
| Iron (Fe), % | 0 to 0.35 | |
| 61.8 to 64 |
| Magnesium (Mg), % | 4.0 to 5.0 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0.2 to 0.5 | |
| 0 to 0.6 |
| Nickel (Ni), % | 0 | |
| 36 |
| Phosphorus (P), % | 0 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.1 |
| Residuals, % | 0 to 0.15 | |
| 0 |