5254 Aluminum vs. EN AC-51100 Aluminum
Both 5254 aluminum and EN AC-51100 aluminum are aluminum alloys. Their average alloy composition is basically identical. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is 5254 aluminum and the bottom bar is EN AC-51100 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 68 |
| Elongation at Break, % | 3.4 to 22 | |
| 4.5 |
| Fatigue Strength, MPa | 110 to 160 | |
| 58 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 240 to 350 | |
| 160 |
| Tensile Strength: Yield (Proof), MPa | 100 to 270 | |
| 80 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 170 |
| Melting Completion (Liquidus), °C | 640 | |
| 640 |
| Melting Onset (Solidus), °C | 590 | |
| 620 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 130 | |
| 130 |
| Thermal Expansion, µm/m-K | 24 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 32 | |
| 34 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.8 | |
| 8.7 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1180 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 to 41 | |
| 6.0 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 73 to 550 | |
| 47 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 51 | |
| 51 |
| Strength to Weight: Axial, points | 25 to 37 | |
| 17 |
| Strength to Weight: Bending, points | 32 to 41 | |
| 25 |
| Thermal Diffusivity, mm2/s | 52 | |
| 53 |
| Thermal Shock Resistance, points | 10 to 16 | |
| 7.3 |
Alloy Composition
| Aluminum (Al), % | 94.4 to 96.8 | |
| 94.5 to 97.5 |
| Chromium (Cr), % | 0.15 to 0.35 | |
| 0 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 to 0.050 |
| Iron (Fe), % | 0 to 0.45 | |
| 0 to 0.55 |
| Magnesium (Mg), % | 3.1 to 3.9 | |
| 2.5 to 3.5 |
| Manganese (Mn), % | 0 to 0.010 | |
| 0 to 0.45 |
| Silicon (Si), % | 0 to 0.45 | |
| 0 to 0.55 |
| Titanium (Ti), % | 0 to 0.050 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.15 |