5449 Aluminum vs. AS41A Magnesium
5449 aluminum belongs to the aluminum alloys classification, while AS41A magnesium belongs to the magnesium alloys.
For each property being compared, the top bar is 5449 aluminum and the bottom bar is AS41A magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 45 |
| Elongation at Break, % | 4.0 to 17 | |
| 11 |
| Fatigue Strength, MPa | 78 to 120 | |
| 100 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 17 |
| Shear Strength, MPa | 130 to 190 | |
| 130 |
| Tensile Strength: Ultimate (UTS), MPa | 210 to 330 | |
| 230 |
| Tensile Strength: Yield (Proof), MPa | 91 to 260 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 370 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 110 |
| Melting Completion (Liquidus), °C | 650 | |
| 620 |
| Melting Onset (Solidus), °C | 590 | |
| 570 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 1000 |
| Thermal Conductivity, W/m-K | 140 | |
| 68 |
| Thermal Expansion, µm/m-K | 23 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 35 | |
| 17 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 92 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 12 |
| Density, g/cm3 | 2.8 | |
| 1.6 |
| Embodied Carbon, kg CO2/kg material | 8.5 | |
| 23 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1180 | |
| 980 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 29 | |
| 21 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 60 to 480 | |
| 220 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 50 | |
| 72 |
| Strength to Weight: Axial, points | 22 to 33 | |
| 38 |
| Strength to Weight: Bending, points | 29 to 39 | |
| 50 |
| Thermal Diffusivity, mm2/s | 56 | |
| 41 |
| Thermal Shock Resistance, points | 9.4 to 15 | |
| 14 |
Alloy Composition
| Aluminum (Al), % | 94.1 to 97.8 | |
| 3.5 to 5.0 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 to 0.060 |
| Iron (Fe), % | 0 to 0.7 | |
| 0 |
| Magnesium (Mg), % | 1.6 to 2.6 | |
| 92.8 to 95.8 |
| Manganese (Mn), % | 0.6 to 1.1 | |
| 0.2 to 0.5 |
| Nickel (Ni), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.4 | |
| 0.5 to 1.5 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.3 | |
| 0 to 0.12 |
| Residuals, % | 0 to 0.15 | |
| 0 |