5454 Aluminum vs. ASTM A356 Grade 2

5454 aluminum belongs to the aluminum alloys classification, while ASTM A356 grade 2 belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 5454 aluminum and the bottom bar is ASTM A356 grade 2.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 61 to 93
150
Elastic (Young's, Tensile) Modulus, GPa 69
190
Elongation at Break, % 2.3 to 18
25
Fatigue Strength, MPa 83 to 160
200
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 26
73
Tensile Strength: Ultimate (UTS), MPa 230 to 350
510
Tensile Strength: Yield (Proof), MPa 97 to 290
270

Thermal Properties

Latent Heat of Fusion, J/g 400
250
Maximum Temperature: Mechanical, °C 190
410
Melting Completion (Liquidus), °C 650
1470
Melting Onset (Solidus), °C 600
1430
Specific Heat Capacity, J/kg-K 900
470
Thermal Conductivity, W/m-K 130
51
Thermal Expansion, µm/m-K 24
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 34
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 110
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
2.4
Density, g/cm3 2.7
7.9
Embodied Carbon, kg CO2/kg material 8.6
1.5
Embodied Energy, MJ/kg 150
20
Embodied Water, L/kg 1180
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.3 to 34
110
Resilience: Unit (Modulus of Resilience), kJ/m3 68 to 590
190
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 50
24
Strength to Weight: Axial, points 23 to 36
18
Strength to Weight: Bending, points 30 to 41
18
Thermal Diffusivity, mm2/s 55
14
Thermal Shock Resistance, points 10 to 16
15

Alloy Composition

Aluminum (Al), % 94.5 to 97.1
0
Carbon (C), % 0
0 to 0.25
Chromium (Cr), % 0.050 to 0.2
0
Copper (Cu), % 0 to 0.1
0
Iron (Fe), % 0 to 0.4
97.7 to 99.55
Magnesium (Mg), % 2.4 to 3.0
0
Manganese (Mn), % 0.5 to 1.0
0 to 0.7
Molybdenum (Mo), % 0
0.45 to 0.65
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0 to 0.25
0 to 0.6
Sulfur (S), % 0
0 to 0.030
Titanium (Ti), % 0 to 0.2
0
Zinc (Zn), % 0 to 0.25
0
Residuals, % 0 to 0.15
0