5454 Aluminum vs. C17000 Copper

5454 aluminum belongs to the aluminum alloys classification, while C17000 copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 5454 aluminum and the bottom bar is C17000 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 69
120
Elongation at Break, % 2.3 to 18
1.1 to 31
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 26
45
Shear Strength, MPa 140 to 200
320 to 750
Tensile Strength: Ultimate (UTS), MPa 230 to 350
490 to 1310
Tensile Strength: Yield (Proof), MPa 97 to 290
160 to 1140

Thermal Properties

Latent Heat of Fusion, J/g 400
230
Maximum Temperature: Mechanical, °C 190
270
Melting Completion (Liquidus), °C 650
980
Melting Onset (Solidus), °C 600
870
Specific Heat Capacity, J/kg-K 900
390
Thermal Conductivity, W/m-K 130
110
Thermal Expansion, µm/m-K 24
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 34
22
Electrical Conductivity: Equal Weight (Specific), % IACS 110
22

Otherwise Unclassified Properties

Density, g/cm3 2.7
8.8
Embodied Carbon, kg CO2/kg material 8.6
8.7
Embodied Energy, MJ/kg 150
140
Embodied Water, L/kg 1180
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.3 to 34
4.2 to 390
Resilience: Unit (Modulus of Resilience), kJ/m3 68 to 590
110 to 5420
Stiffness to Weight: Axial, points 14
7.6
Stiffness to Weight: Bending, points 50
19
Strength to Weight: Axial, points 23 to 36
15 to 41
Strength to Weight: Bending, points 30 to 41
16 to 30
Thermal Diffusivity, mm2/s 55
32
Thermal Shock Resistance, points 10 to 16
17 to 45

Alloy Composition

Aluminum (Al), % 94.5 to 97.1
0 to 0.2
Beryllium (Be), % 0
1.6 to 1.8
Chromium (Cr), % 0.050 to 0.2
0
Copper (Cu), % 0 to 0.1
96.3 to 98.2
Iron (Fe), % 0 to 0.4
0 to 0.4
Magnesium (Mg), % 2.4 to 3.0
0
Manganese (Mn), % 0.5 to 1.0
0
Nickel (Ni), % 0
0.2 to 0.6
Silicon (Si), % 0 to 0.25
0 to 0.2
Titanium (Ti), % 0 to 0.2
0
Zinc (Zn), % 0 to 0.25
0
Residuals, % 0
0 to 0.5